介绍了热压扩散结合法制备 Ｂ／ Ａｌ 复合板材的工艺过程，研究了热压工艺参数对 Ｂ／ Ａｌ 复合板材性能的影响，获得了热压扩散结合法制备 Ｂ／ Ａｌ 复合板材比较理想的工艺参数，得到了拉伸强度σｂ ＝ １ ２８０ Ｍ Ｐａ 、弹性模量 Ｅ＝ ２３３ Ｇ Ｐａ 的 Ｂ／ Ａｌ 复合板材。
The process of preparing B / Al composite sheet by hot-pressure diffusion bonding was introduced. The effect of hot-pressing process parameters on the properties of B / Al composite sheet was studied. The ideal process of preparing B / Al composite sheet by hot- Parameters, B / Al composite sheet with tensile strength σb = 1,280 Mpa and elastic modulus E = 233 G Pa was obtained.