In this paper, a novel near-net-shape forming process, continuous semisolid extrusion process (CSEP) of AZ31 alloy was proposed, and the dynamical solidification behaviors and metal flow during the process were firstly investigated. During casting AZ31 alloy by this process, non-uniform microstructure distributions and non-equilibrium solidification region near the roll surface were found in the roll-shoe gap. Microstructural evolution from dendrite to rosette and spherical grains was observed during the casting by CSEP. Casting temperature, roll-shoe gap width and cooling ability have great effect on casting process and metal flow, so these factors should be carefully controlled, a proper casting temperature of 710-750℃ is suggested. The white α phases were strongly stretched during the processing, and the remnant liquids are correspondingly distributes along the solid phase boundaries and also show stripped lines.
In this paper, a novel near-net-shape forming process, continuous semisolid extrusion process (CSEP) of AZ31 alloy was proposed, and the dynamical solidification behaviors and metal flow during the process were investigated. During casting AZ31 alloy by this process, non-uniform microstructure distributions and non-equilibrium solidification regions near the roll surface were found in the roll-shoe gap. Microstructural evolution from dendrite to rosette and spherical grains was observed during the casting by CSEP. Casting temperature, roll-shoe gap width and cooling ability have great effect on casting process and metal flow, so these factors should be carefully controlled, a proper casting temperature of 710-750 ℃ is suggested. The white α phases were strongly stretched during the processing, and the remnant liquids are correspondingly distributes along the solid phase boundaries and also show stripped lines.