摘要：随着高层建筑的不断增多，轻集料混凝土小型空心砌块成为近年来使用较多的非承重新型墙体材料，但由于砌块强度等级低、吸水率高、收缩变形大，且沿用传统的墙体砌筑方法与墙面抹灰工艺，经常出现墙体裂缝，由裂缝引起渗漏、墙面抹灰空鼓、开裂等质量问题。要根本解决轻集料混凝土小型空心砌块墙体裂缝问题就必须从砌体裂缝的形成原因入手。
关键词：高层建筑混凝土墙体裂缝渗漏温度
Abstract: with the increasing of high-rise buildings, lightweight aggregate concrete small hollow blocks become in recent years used more blame bearing new wall materials, but because block intensity level is low, bibulous rate is high, the contraction deformation of big, and adhere to the traditional building method of the wall plastering technology with metope, often appear wall cracks, caused by leakage crack, metope empty drum, plastering quality problem such as craze. To fundamentally solve lightweight aggregate concrete hollow blocks wall cracks small must be the cause of formation of the masonry structure from the start.
Keywords: high building concrete wall temperature crack leakage
中图分类号：[TU208.3]文献标识码：A 文章编号： 墙体裂缝产生的形式和种类很多，主要表现形式为不同材料间的界面裂缝，墙体中间的水平裂缝、竖向裂缝，山墙面的阶梯式裂缝。裂缝产生的原因主要分为四类：一是温度裂缝，二是干燥收缩裂缝，三是设计构造原因产生的裂缝，四是施工质量造成的裂缝。还有温度差和干缩共同作用也会产生裂缝，具体原因分析如下：
1、温度裂缝温度裂缝是因日照及昼夜温差、室内外温差、季节温差所产生的温度变化，引起的材料热胀、冷缩。有相关资料显示：如果结构在温度变化时受到约束而不能自由变形时，则将在结构中产生附加应力，使砌体结构产生裂缝。在框架结构中，框架围护填充墙多采用轻集料混凝土小型空心砌块来填充，砌块壁较薄，中间为三排孔或四排孔，空心率大，且温度线膨胀系数为1.0×10.5-5/℃，与砖砌体的线膨胀系数0.5×10-5/℃相差近一倍， 当温度变化时，小型空心砌块砌体对温度的敏感性比砖砌体高， 更容易因温度变形引起裂缝。尽管轻集料混凝土小型空心砌块砌筑墙体的线胀系数与屋面顶盖混凝土板的线胀系数没有大的差别， 但在夏季阳光照射下两者之间还是存在一定的温差。当外界温度升高时，混凝土顶盖变形大，墙体变形相对较小，使屋盖受压，墙体受拉、受剪，导致两者温度变形不协调，产生墙体裂缝。温度裂缝是有规律性的：如框架梁下沿砌块顶部水平裂缝，门窗洞边的角裂缝等表现为两端重中间轻，顶部重逐渐往下减轻，阳面重阴面轻。2、干缩裂缝
轻集料混凝土小型空心砌块是混凝土拌和料经浇注、振捣、养护而成。混凝土在硬化过程中逐渐失水而干缩，其干缩量因材料和成型质量而异， 收缩约在0.35mm/m至0.5mm/m之间，并随时间增长而逐渐减小。以普通混凝土砌块为例，在自然养护条件下，成型28d 后，收缩趋于稳定，其干缩率为0.03%至0.035%，含水率为50%至60％， 砌成砌体后，在正常使用条件下，含水率继续下降，可达10％左右，其干缩率为0.018%至0.07%，干缩率的大小与砌块上墙时含水率有关。所以砌块含水率是产生干缩裂缝的主要因素，如果砌块上墙时含水率较大，经过一段时间后，砌体含水率降低，便出现干缩裂縫。墙面上框架柱和砌块填充墙之间沿柱两侧的垂直裂缝以及山墙面上圈粱上下和砌块结合面上的水平裂缝，均是由于两种构件因收缩不协调而引起的。对于干缩已趋稳定的轻集料混凝土小型空心砌块砌体，如再次被浸湿后，会再次发生干缩，通常称为第二干缩。普通混凝土砌块的第二干缩，其稳定时间比成型硬化过程的第一干缩时间要短，一般约为15d。第二干缩的收缩率约为第一干缩的80％。即使已砌筑完工的砌体无干缩裂缝，但当砌块因某种原因再次被水浸湿后仍会出现第二干缩，砌体仍可能产生裂缝。
砌块上墙后在砌体内部产生一定的收缩应力，当砌体的抗拉、抗剪强度不足以抵抗收缩应力时，就会产生裂缝。因砌块干缩而引起的墙体裂缝，在内外墙均可能出现。干缩裂缝形态一般有四种，一是在墙体中部出现的阶梯形裂缝，二是环块材周边灰缝的裂缝，三是在外墙多反映在窗下墙，出现竖向均匀裂缝，四是在山墙等大墙面出现竖向、水平向裂缝。3、设计构造造成的裂缝
在遇到下列情况时不采取有效的构造措施也会出现墙体裂缝
a、砌块墙体砌筑过长、过高时，应采取加强构造措施。
b、门窗洞及预留洞的四角处属于应力集中区，应采取合理连接构造措施。c、墙面开槽、开洞安装管线、线盒及插座等，应提出细部处理要求。d、墙面吊挂重物处时，应做加固处理。
4、施工质量造成的裂缝
施工中不注意其施工要点，未能对砌块的施工给予足够重视，未能完全掌握其性能，不按规范施工，是引起砌体裂缝的主要原因。第一、由于砌块砌体和混凝土构件的变形值不同，加上末按要求留置墙柱拉结筋或拉结筋长度不足，砌筑过程中工人因砌体皮数不符合模数而造成砌体与拉结筋无法锚固，砌筑时未按要求将拉结筋砌入墙体内，所以在建筑物的两端柱与墙连结的部位会产生裂缝。第二、砌块含水率控制不好，上墙时含水量过大或雨期施工淋湿砌块，墙体因干缩引起开裂。第三、砌块排列不合理，未按规定接槎砌筑，水平、竖缝厚薄不均且砂浆不饱满，砂浆和易性、保水性能差等。第四、墙体砌筑时砂浆铺灰面过大，砂浆失水干燥影响粘结强度。第五、未按规定砌筑顶砖。对于轻集料混凝土小型空心砌块顶砖必须要隔7d 才能砌筑， 目的是等下部砌体砂浆已硬结， 墙体不再由于自重而引起沉降。第六、砌块不按底面（盲孔）朝上反砌。第七、抹灰前基底未清理干净，砌体完成后未有合理的时间间隔便进行抹灰。
针对上述裂缝产生原因制定具体预防措施：
1、为避免室内外温差造成的墙体裂缝，必须做好屋面保温和外墙外保温，控制屋面板与墙体的温差及外墙内外两侧的温差是减少温度应力的有效措施。
2、要避免砌块产生干缩裂缝首先是必须确保砌块在厂内的养护龄期已经达到28天。一般刚出厂的砌块稳定性较差，干缩变形的特征是早期发展比较快，以后逐步变慢。因此，使用前应确保材料已达到使用龄期，体积已基本稳定，干缩变形较小。其次是控制砌块的含水率。在砌块上墙前必须做好防水措施，不宜洒水淋湿，尽量避免雨期施工淋湿砌块，以防相对含水率超标。3、设计构造的控制措施：a、墙体长度超过层高2倍或墙体长度大于4.0m 时，墙中应设置钢筋混凝土构造柱。墙高大于4m 时， 应在墙体半高处设置沿墙全长贯通的钢筋混凝土水平连系梁，连系梁钢筋与构造柱相连。b、砌块墙体的门窗过梁应与墙体厚度和砌块高度相匹配，过梁入墙长度应不小于600mm，否则应锚入柱内或采取其他措施。窗台处应加设现浇或预制钢筋混凝土压顶。c、砌筑砌块墙体时应设置拉结钢筋与钢筋混凝土柱、墙可靠连接，拉结钢筋应不少于2φ6钢筋，沿钢筋混凝土墙或柱全高每隔3 皮砌块或不超过600mm设置一道。4、采用正确的施工方法保证砌筑质量避免产生墙体裂缝：按照砌块的组砌方法将砌块盲孔面朝上反砌于墙上。砌筑时应尽量采用主规格砌块，并应清除砌块表面污物及底部毛边，尽量对孔搭砌，砌体的灰缝应横平竖直，灰缝饱满，以确保墙体质量。每天砌高度不得超过1.8m,停砌后的墙体应处理好施工缝，将浮灰清理干净。墙顶砌体必须间隔7d顶紧砌筑，避免引起接合部位开裂。严格控制墙体孔洞预留及开槽的处理，避免削弱墙体强度，以确保墙体的整体性。5、内外墙粉刷节点处理：在砌块墙体与混凝土结构接触界面设宽200mm的钢丝网或耐碱玻纤网格布， 每边各搭接100mm。墙中安装管道处，沿管道方向布置宽为600mm的钢丝网或耐碱玻纤网格布，防止墙体粉刷层产生水平裂缝和竖向裂缝。消防栓等方形洞口四角呈45°布置宽600mm 的钢丝网或耐碱玻纤网格布，防止粉刷层开裂。总之，虽然轻集料混凝土小型空心砌块墙体开裂的原因较多，但是，只要严格执行有关砌体规范，从生产、设计、施工等多方综合防治，针对砌体裂缝以防为主，精心设计，规范施工，采取有效的控制措施，轻集料混凝土小型空心砌块墙体裂缝的质量通病是可以控制的。
关键词：高层建筑混凝土墙体裂缝渗漏温度
Abstract: with the increasing of high-rise buildings, lightweight aggregate concrete small hollow blocks become in recent years used more blame bearing new wall materials, but because block intensity level is low, bibulous rate is high, the contraction deformation of big, and adhere to the traditional building method of the wall plastering technology with metope, often appear wall cracks, caused by leakage crack, metope empty drum, plastering quality problem such as craze. To fundamentally solve lightweight aggregate concrete hollow blocks wall cracks small must be the cause of formation of the masonry structure from the start.
Keywords: high building concrete wall temperature crack leakage
中图分类号：[TU208.3]文献标识码：A 文章编号： 墙体裂缝产生的形式和种类很多，主要表现形式为不同材料间的界面裂缝，墙体中间的水平裂缝、竖向裂缝，山墙面的阶梯式裂缝。裂缝产生的原因主要分为四类：一是温度裂缝，二是干燥收缩裂缝，三是设计构造原因产生的裂缝，四是施工质量造成的裂缝。还有温度差和干缩共同作用也会产生裂缝，具体原因分析如下：
1、温度裂缝温度裂缝是因日照及昼夜温差、室内外温差、季节温差所产生的温度变化，引起的材料热胀、冷缩。有相关资料显示：如果结构在温度变化时受到约束而不能自由变形时，则将在结构中产生附加应力，使砌体结构产生裂缝。在框架结构中，框架围护填充墙多采用轻集料混凝土小型空心砌块来填充，砌块壁较薄，中间为三排孔或四排孔，空心率大，且温度线膨胀系数为1.0×10.5-5/℃，与砖砌体的线膨胀系数0.5×10-5/℃相差近一倍， 当温度变化时，小型空心砌块砌体对温度的敏感性比砖砌体高， 更容易因温度变形引起裂缝。尽管轻集料混凝土小型空心砌块砌筑墙体的线胀系数与屋面顶盖混凝土板的线胀系数没有大的差别， 但在夏季阳光照射下两者之间还是存在一定的温差。当外界温度升高时，混凝土顶盖变形大，墙体变形相对较小，使屋盖受压，墙体受拉、受剪，导致两者温度变形不协调，产生墙体裂缝。温度裂缝是有规律性的：如框架梁下沿砌块顶部水平裂缝，门窗洞边的角裂缝等表现为两端重中间轻，顶部重逐渐往下减轻，阳面重阴面轻。2、干缩裂缝
轻集料混凝土小型空心砌块是混凝土拌和料经浇注、振捣、养护而成。混凝土在硬化过程中逐渐失水而干缩，其干缩量因材料和成型质量而异， 收缩约在0.35mm/m至0.5mm/m之间，并随时间增长而逐渐减小。以普通混凝土砌块为例，在自然养护条件下，成型28d 后，收缩趋于稳定，其干缩率为0.03%至0.035%，含水率为50%至60％， 砌成砌体后，在正常使用条件下，含水率继续下降，可达10％左右，其干缩率为0.018%至0.07%，干缩率的大小与砌块上墙时含水率有关。所以砌块含水率是产生干缩裂缝的主要因素，如果砌块上墙时含水率较大，经过一段时间后，砌体含水率降低，便出现干缩裂縫。墙面上框架柱和砌块填充墙之间沿柱两侧的垂直裂缝以及山墙面上圈粱上下和砌块结合面上的水平裂缝，均是由于两种构件因收缩不协调而引起的。对于干缩已趋稳定的轻集料混凝土小型空心砌块砌体，如再次被浸湿后，会再次发生干缩，通常称为第二干缩。普通混凝土砌块的第二干缩，其稳定时间比成型硬化过程的第一干缩时间要短，一般约为15d。第二干缩的收缩率约为第一干缩的80％。即使已砌筑完工的砌体无干缩裂缝，但当砌块因某种原因再次被水浸湿后仍会出现第二干缩，砌体仍可能产生裂缝。
砌块上墙后在砌体内部产生一定的收缩应力，当砌体的抗拉、抗剪强度不足以抵抗收缩应力时，就会产生裂缝。因砌块干缩而引起的墙体裂缝，在内外墙均可能出现。干缩裂缝形态一般有四种，一是在墙体中部出现的阶梯形裂缝，二是环块材周边灰缝的裂缝，三是在外墙多反映在窗下墙，出现竖向均匀裂缝，四是在山墙等大墙面出现竖向、水平向裂缝。3、设计构造造成的裂缝
在遇到下列情况时不采取有效的构造措施也会出现墙体裂缝
a、砌块墙体砌筑过长、过高时，应采取加强构造措施。
b、门窗洞及预留洞的四角处属于应力集中区，应采取合理连接构造措施。c、墙面开槽、开洞安装管线、线盒及插座等，应提出细部处理要求。d、墙面吊挂重物处时，应做加固处理。
4、施工质量造成的裂缝
施工中不注意其施工要点，未能对砌块的施工给予足够重视，未能完全掌握其性能，不按规范施工，是引起砌体裂缝的主要原因。第一、由于砌块砌体和混凝土构件的变形值不同，加上末按要求留置墙柱拉结筋或拉结筋长度不足，砌筑过程中工人因砌体皮数不符合模数而造成砌体与拉结筋无法锚固，砌筑时未按要求将拉结筋砌入墙体内，所以在建筑物的两端柱与墙连结的部位会产生裂缝。第二、砌块含水率控制不好，上墙时含水量过大或雨期施工淋湿砌块，墙体因干缩引起开裂。第三、砌块排列不合理，未按规定接槎砌筑，水平、竖缝厚薄不均且砂浆不饱满，砂浆和易性、保水性能差等。第四、墙体砌筑时砂浆铺灰面过大，砂浆失水干燥影响粘结强度。第五、未按规定砌筑顶砖。对于轻集料混凝土小型空心砌块顶砖必须要隔7d 才能砌筑， 目的是等下部砌体砂浆已硬结， 墙体不再由于自重而引起沉降。第六、砌块不按底面（盲孔）朝上反砌。第七、抹灰前基底未清理干净，砌体完成后未有合理的时间间隔便进行抹灰。
针对上述裂缝产生原因制定具体预防措施：
1、为避免室内外温差造成的墙体裂缝，必须做好屋面保温和外墙外保温，控制屋面板与墙体的温差及外墙内外两侧的温差是减少温度应力的有效措施。
2、要避免砌块产生干缩裂缝首先是必须确保砌块在厂内的养护龄期已经达到28天。一般刚出厂的砌块稳定性较差，干缩变形的特征是早期发展比较快，以后逐步变慢。因此，使用前应确保材料已达到使用龄期，体积已基本稳定，干缩变形较小。其次是控制砌块的含水率。在砌块上墙前必须做好防水措施，不宜洒水淋湿，尽量避免雨期施工淋湿砌块，以防相对含水率超标。3、设计构造的控制措施：a、墙体长度超过层高2倍或墙体长度大于4.0m 时，墙中应设置钢筋混凝土构造柱。墙高大于4m 时， 应在墙体半高处设置沿墙全长贯通的钢筋混凝土水平连系梁，连系梁钢筋与构造柱相连。b、砌块墙体的门窗过梁应与墙体厚度和砌块高度相匹配，过梁入墙长度应不小于600mm，否则应锚入柱内或采取其他措施。窗台处应加设现浇或预制钢筋混凝土压顶。c、砌筑砌块墙体时应设置拉结钢筋与钢筋混凝土柱、墙可靠连接，拉结钢筋应不少于2φ6钢筋，沿钢筋混凝土墙或柱全高每隔3 皮砌块或不超过600mm设置一道。4、采用正确的施工方法保证砌筑质量避免产生墙体裂缝：按照砌块的组砌方法将砌块盲孔面朝上反砌于墙上。砌筑时应尽量采用主规格砌块，并应清除砌块表面污物及底部毛边，尽量对孔搭砌，砌体的灰缝应横平竖直，灰缝饱满，以确保墙体质量。每天砌高度不得超过1.8m,停砌后的墙体应处理好施工缝，将浮灰清理干净。墙顶砌体必须间隔7d顶紧砌筑，避免引起接合部位开裂。严格控制墙体孔洞预留及开槽的处理，避免削弱墙体强度，以确保墙体的整体性。5、内外墙粉刷节点处理：在砌块墙体与混凝土结构接触界面设宽200mm的钢丝网或耐碱玻纤网格布， 每边各搭接100mm。墙中安装管道处，沿管道方向布置宽为600mm的钢丝网或耐碱玻纤网格布，防止墙体粉刷层产生水平裂缝和竖向裂缝。消防栓等方形洞口四角呈45°布置宽600mm 的钢丝网或耐碱玻纤网格布，防止粉刷层开裂。总之，虽然轻集料混凝土小型空心砌块墙体开裂的原因较多，但是，只要严格执行有关砌体规范，从生产、设计、施工等多方综合防治，针对砌体裂缝以防为主，精心设计，规范施工，采取有效的控制措施，轻集料混凝土小型空心砌块墙体裂缝的质量通病是可以控制的。