Ｎ＿２吸附等温线及ＢＪＨ脱附孔分布结果表明：当钛含量合适时，所合成的Ｔｉ－Ｓｉ沸石具有非常均匀的孔结构。ＴＳ－１沸石（ＺＳＭ—５型）的ＢＥＴ表面积为３８６—４２３ｍ￣２／ｇ，ＴＳ－２沸石（ＺＳＭ－１１型）的ＢＥＴ表面积为３５５—４５６ｍ￣２／ｇ，且均随合成沸石中钛含量增加而呈下降的趋势。吸附结果表明Ｔｉ－Ｓｉ沸石均有明显的疏水性，其正己烷的吸附量明显高于环己烷，随钛含量不同而发生变化，但其Ｈ＿２Ｏ＿２的吸附量却随钛含量增加而显著增大。ＮＨ＿３—ＴＰＤ试验表明，Ｔｉ－Ｓｉ沸石表面酸性相当弱，根本不存在强酸中心。
The results of N 2 adsorption isotherm and BJH desorption pore distribution show that the Ti-Si zeolite synthesized has a very uniform pore structure when the titanium content is suitable. The BET surface area of TS-1 zeolite (ZSM-5 type) is 386-423 m 2 / g and that of TS-2 zeolite (ZSM-11 type) is 355-456 m 2 / g, Titanium content increased and declined. Adsorption results show that Ti-Si zeolite has obvious hydrophobicity. The adsorption amount of n-hexane is obviously higher than that of cyclohexane, and changes with the content of titanium. However, the adsorption amount of H 2 O 2 increases significantly with the increase of titanium content . NH_3-TPD test shows that the surface of Ti-Si zeolite is rather weak and there is no strong acid center at all.