The adsorption behaviors and dispersing properties of polycarboxylate superplasticizer (PCE) with different functional groups were systematically analyzed to reveal the theory and methods of modifying PCE molecular structures and regulating PCE performanc
【机 构】
：
School of Civil Engineering, Suzhou University of Science and Technology, Suzhou 215011, China;State
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The adsorption behaviors and dispersing properties of polycarboxylate superplasticizer (PCE) with different functional groups were systematically analyzed to reveal the theory and methods of modifying PCE molecular structures and regulating PCE performances. By substituting carboxylic groups with sulfonic groups, ester groups or acylamino groups, respectively, modified PCEs with different functional groups were synthesized. Results show that introducing low amount of ester groups or sulfonic groups into the PCE molecules has no negative effects on the fluidity of cement paste, while introducing acylamino groups into PCE molecules significantly weakens the fluidity of cement paste. At low amount (when the molar ratio of sodium methallyl sulfonate to TPEG is lower than 0.4), the rapid adsorption of sulfonic groups onto the cement particles contributes to the high dispersing performance of the sulfonic group modified PCEs. When the substitution ratio of acrylic acid by sulfonic acid is higher than 0.4, the viscosity and the yield stress of cement paste increases sharply. Redundant sulfonic groups lead to the excessive charge density of the PCE, which contributes to the inhomogeneous adsorption on the cement grains and hence results in the decline of the dispersing performance. Substitution of carboxylic group by acylamino group or ester group slightly changes the viscosity as well as the yield stress of cement paste. Introducing sulfonic group into PCE molecule improves the adsorption behavior of PCEs, while introducing ester group or acylamino group into PCE depresses the adsorption properties.
其他文献
Eu3+ ion doped cubic Na5Lu9F32 single crystals with high quality were synthesized by a modified Bridgman method by using a high 70-90 ℃/cm temperature gradient for cross solid-liquid interface.The optical spectroscopic investigations of the obtained singl
Five kinds of mortars with density grades of 500, 600, 700, 800, and 900 kg/m3 were prepared. Their thermal conductivity and compressive strength were measured, and the morphological changes before and after simulated tunnel fire were observed. To investi
Influence mechanism of sulfide ions (S2-) during manganese electrodeposition from sulphate electrolyte was investigated. Under the experimental conditions, S2- ion concentration and electrolyte pH represented significant multiple effects on the cathode cu
The viscoplasticity and compressive strength of cement with high erosion performance were studied. The influences of curing temperature and content of ground granulated blast furnace slag (GGBFS) on these performances of the medium heat cement (including
The scope of the present paper is to understand the effects of crystalline admixture on the self-healing capacity of the cementitious composites. Previous studies were examined and a conclusion was drawn to the effect that different additives to crystalli
The internal curing effect of superabsorbent polymer (SAP) on the properties of high performance concrete (HPC) under marine wetting and drying cycles (WD cycles) was investigated. Compressive strength, hydration and chloride migration were experimentally
The binder properties were determined in accordance with Chinese standard such as ductility test, which allowed to measure the distance in centimeters that a standard briquette of asphalt had been stretched before breaking. Then, penetration test was carr
An effect of heating and stirring in a facile wet chemical route to synthesize entangled nano-fibrous mesh of doped polyaniline (PANI) was reported. The structural, morphological, and optical properties of PANI nano-fibers were found to be dependent on sy
A dual-receptor targeting delivery system based on acid-cleavage hydrazone bond was developed in the study. The characters of CMCS-hyd-CUR-EGFR- mAb were identified. The in vitro release studies revealed that this drug delivery system was acid-sensitive,
Bis[2-(3,4-epoxycyclohexyl)ethyl]octamethyltetrasiloxane is also called diepoxycyclohexylethyl octamethyltetrasiloxane. In the present paper, diepoxycyclohexylethyl octamethyltetrasiloxane was synthesized, and the synthesized product was characterized by