The internal curing effect of superabsorbent polymer (SAP) on the properties of high performance concrete (HPC) under marine wetting and drying cycles (WD cycles) was investigated. Compressive strength, hydration and chloride migration were experimentally
【机 构】
：
State Key Laboratory of Silicate Materials for Architecture, Wuhan University of Technology, Wuhan 4
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The internal curing effect of superabsorbent polymer (SAP) on the properties of high performance concrete (HPC) under marine wetting and drying cycles (WD cycles) was investigated. Compressive strength, hydration and chloride migration were experimentally investigated and the results were evaluated by compasison with those under fresh water curing (FW). Water absorption and porosity were also evaluated only under WD cycles. The results showed the important influence of wetting and drying cycles on the properties of SAP modified HPC properties. Carefully designed, SAP minimized the long-term compressive strength of HPC under marine WD cycles. The hydration rate was faster in the initial curing, but became lower as compared with that cured in FW. In addition, SAP improved the long-term water absorption resistance and chloride migration resistance of HPC under marine WD cycles. The examination of the porosity showed a lower increase of the volume of capillary pores in SAP modified HPC under long term WD cycles compared with that without SAP. Therefore, internal curing by SAP could improve the durability properties of HPC under marine WD cycles.
其他文献
Based on an advanced technology, randomly-aligned subwavelength structures (SWSs) were obtained by a metal-nanodot-induced one-step self-masking reactive-ion-etching process on a fused silica surface. Metal-fluoride (mainly ferrous-fluoride) nanodots indu
To explore the complex thermal-mechanical-chemical behavior in the solid-liquid cast-roll bonding (SLCRB) of Cu/Al cladding strip,numerical simulations were conducted from both macro and micro scales.In macro-scale,with birth and death element method,a th
An electro-deposition method has been recently proposed to repair cracked reinforced concrete. To evaluate the corrosion resistance of the reinforcing steel in cracked concrete, three different parameters including type of auxiliary electrode, electrode d
Cement pastes containing 0％, 15％, 25％ and 35％ fly ash were prepared. After being cured for 90 days, all fly ash blended cement pastes were crushed and ground into powders with a particle size less than 80 μm and then the powders were immersed in alkali so
V-Cr-Al-O nanospheres were successfully synthesized using V2O5, Al(OH)3, CrO3, and H2C2O4·H2O as the starting materials by a facile one-pot hydrothermal approach. Several techniques containing X-ray powder diffraction, hydrogen temperature programmed redu
Eu3+ ion doped cubic Na5Lu9F32 single crystals with high quality were synthesized by a modified Bridgman method by using a high 70-90 ℃/cm temperature gradient for cross solid-liquid interface.The optical spectroscopic investigations of the obtained singl
Five kinds of mortars with density grades of 500, 600, 700, 800, and 900 kg/m3 were prepared. Their thermal conductivity and compressive strength were measured, and the morphological changes before and after simulated tunnel fire were observed. To investi
Influence mechanism of sulfide ions (S2-) during manganese electrodeposition from sulphate electrolyte was investigated. Under the experimental conditions, S2- ion concentration and electrolyte pH represented significant multiple effects on the cathode cu
The viscoplasticity and compressive strength of cement with high erosion performance were studied. The influences of curing temperature and content of ground granulated blast furnace slag (GGBFS) on these performances of the medium heat cement (including
The scope of the present paper is to understand the effects of crystalline admixture on the self-healing capacity of the cementitious composites. Previous studies were examined and a conclusion was drawn to the effect that different additives to crystalli