The K2Ti4O9 whiskers were chosen for the catalyst carrier, TiO2/potassium titanate photocatalyst was prepared by Sol-gel method. The product was characterated by X-ray diffraction and SEM. EDS shows that, the main peck included Ti, O, and K in potassium titanate whisker. The main peak of K disappeared and the peaks of Ti, O stayed after whisker was covered. It directed that the surface of sample was covered by TiO2. XRD shows that diffraction peak appeared, which was corresponded to the peak of anatase TiO2. In the reaction device of photochemistry, using middle-pressure mercury lamp as illumination, rhodamine B as simulant pollutant, the photocatalytic performance of TiO2/potassium titanate was studied. Under the same conditions, the lower pH, the larger illuminance, the higher temperature, the greater aeration quantum and the lower initial concentration of rhodamine B, the higher decoloration rate was got. Under our experiment conditions: pH 6, the illuminance of 250W, the temperature of 313K, and the aeration quantum of 2.0L/min. When the concentration of rhodamine B was 8mg/L The photocatalyst of TiO2/potassium titanate was 0.01g/L. The decoloration rate of TiO2/potassium titanate dealt with the rhodamine B reach over 95% in 160min, and compare with TiO2, the decoloration rate of rhodamine B was improved 0.50~1.91 multiple. TiO2/potassium titanate can be used to treatment of dye wastewater.
The K2Ti4O9 whiskers were chosen for the catalyst carrier, TiO2 / potassium titanate photocatalyst was prepared by Sol-gel method. The product was characterated by X-ray diffraction and SEM. EDS shows that, the main peck included Ti, O, and K in The main peak of K disappeared and the peaks of Ti, O stayed after whisker was covered. It directed that the surface of sample was covered by TiO2. which is corresponded to the peak of anatase In the reaction device of photochemistry, using middle-pressure mercury lamp as illumination, rhodamine B as simulant pollutant, the photocatalytic performance of TiO2 / potassium titanate was studied. The lower pH, the larger illuminance, the higher temperature, the greater aeration quantum and the lower initial concentration of rhodamine B, the higher decoloration rate was got. The concentration of rhodamine B was 8 mg / L The photocatalyst of TiO2 / potassium titanate was 0.01 g / L. The decoloration rate of TiO2 / potassium titanate dealt with the rhodamine B reach over 95% in 160min, and compare with TiO2, the decoloration rate of rhodamine B was improved 0.50 ~ 1.91 multiple. TiO2 / potassium titanate can be used to treat of dye wastewater.