【摘 要】
：
我们适应工程上的需要,研究了1Cr18Ni9Ti奥氏体不锈钢在沸腾的高浓度MgCr_2水溶液中的腐蚀疲劳行为。试样从热轧棒材上切取,经1100℃,10min,W.Q.后加工而成,标距部分为直径3
【机 构】
：
中国科学院金属研究所,中国科学院金属研究所,
论文部分内容阅读
我们适应工程上的需要,研究了1Cr18Ni9Ti奥氏体不锈钢在沸腾的高浓度MgCr_2水溶液中的腐蚀疲劳行为。试样从热轧棒材上切取,经1100℃,10min,W.Q.后加工而成,标距部分为直径3长15mm,表面光洁度▽8。又从管材上切取15×3×1.5mm的片状试样,表面光洁度▽6。试验用钢的化学成分(wt-％)为;C 0.05,Mn 1.84,Si 0.53,S 0.021,P 0.026,Cr 18.40,Ni 10.30,Ti 0.45,Fe余量。试验在专用的蠕变-疲劳试验机上进行,交
We adapt to the engineering needs, studied 1Cr18Ni9Ti austenitic stainless steel in boiling high concentrations of MgCr 2 aqueous solution of corrosion fatigue behavior. The sample was cut from the hot rolled bar, after 1100 ℃, 10min, W.Q. After processing from the gauge part of the diameter of 3 length 15mm, surface finish ▽ 8. Also from the pipe cut 15 × 3 × 1.5mm sheet samples, surface finish ▽ 6. The test steel had a chemical composition (wt-%) of C 0.05, Mn 1.84, Si 0.53, S 0.021, P 0.026, Cr 18.40, Ni 10.30, Ti 0.45, Fe balance. Test in a dedicated creep - fatigue test machine, pay
其他文献
由武汉水利电力学院与湖北塑料电线厂协作研制的纯铝MIG焊丝研制成功,于86年10月16日至18日在湖北鄂州市通过成果及产品的技术鉴定。
The pure aluminum MIG welding wire
研究了Al-Li合金为芯体、Al-Mg-Cu-Si合金为包壳的扩散偶,经共挤压及520℃/2h固溶处理后,芯体与包壳间的互扩散现象。实验证明,芯体与包壳间的扩散层——Al(Li-Mg-Cu-Si)的形
大家知道,纯铝不溶于水,因为铝的表面形成了一种薄而坚硬类似盾甲的氧化物,使金属不能与氧进行接触。但是,任何坚硬的盾甲也能找到对付它的矛。苏联哈萨克苏维埃社会主义共
液压技术中,中高压(210kg/cm~2)柱塞泵(马达)是用量最大,应用范围相当广泛的液压元件。目前,美国、日本、瑞典等国已在该种泵(马达)中采用了粉末冶金铁
Hydraulic technolo
少无氧化加热技术是正在发展的一项新技术。它不但可以节约金属,而且可以显著地提高加热质量,减少加工工序,降低成本。同时,是实现精密锻造必不可少的配套工艺和先进技术。
美国挤压珩磨公司采用超声振动磨削方式制造和修整尺寸较小的精细形状石黑电极。它是利用成形工具(预制成所欲加工的形状)作高频(20000Hz)小振幅(0.025mm)振动来捶击处于加
本文主要介绍了在16Mn板材上进行的富氩焊接工艺试验。通过对采用富氩焊接和CO_2焊接的焊接接头进行机械性能试验、疲劳寿命试验、低温冲击韧性试验的对比,找出富氩焊接的最
过去圆钢轧辊车削用的样板一般均采用普通低碳钢板,用人工划线,手工制作。由于车削孔型时样板经常与转动着的轧辊接触,因而磨损较大,长时间使用后无法保证孔型车削精度。近
在自动化加工过程中,自动检测刀具很重要.本文介绍在加工过程中,利用声发射检测钻头破损的方法.图21幅，表3个。
In the automated processing, automatic tool detection is
拐轴是履带车中重要配件。承受弯曲、冲击等多种载荷,对强度和韧性等性能要求很高。以往都用40Cr钢材锻造成型,但锻造拐轴的金属利用率低,工序多,成本高,设备投资大。国内外