热拉试验M.C.Losinski 等曾经报导关于含0.45%—1.65%C的钢种以及各种 Cu-Ni 合金在600—900℃下连续10小时进行拉力试验的情况。其显微组织系用真空装置连续观察到的。W.Barr 等获得了约含0.16%C,1.35%Mn,0.4—0.65%Cr,0.25%Mo 和0.07%V 的有可焊性的钢种在20—400℃范围内进行拉力试验的结果,试验取自110mm 厚的钢板。H.F.Beeghly 得出了含低锰及少量钛或锆的各种非合金钢种.(如0.08—0.23%C,0.08—0.16%Mn,0—0.37%Cu,0.14—0.45%Ti)在20—700℃时热拉试验的结果,此类钢种特别适用于反应器的制造。
Hot Tensile Tests M. C. Losinski et al. Have reported on tensile tests of steel grades containing 0.45% -1.65% C and various Cu-Ni alloys for 10 hours at 600-900 ° C. The microstructure was continuously observed with a vacuum device. W. Barr et al. Obtained results of a tensile test of a solderable steel containing about 0.16% C, 1.35% Mn, 0.4-0.65% Cr, 0.25% Mo and 0.07% V in the range of 20-400 ° C, Test taken from 110mm thick steel. HFBeeghly yields a variety of non-alloyed steels containing low and small amounts of titanium or zirconium (eg 0.08-0.23% C, 0.08-0.16% Mn, 0-0.37% Cu, 0.14-0.45% Ti) The results of the hot-pull test at 700 ° C are particularly suitable for the manufacture of reactors.