【摘 要】
：
以镀银铝粉为高导电填料,硅橡胶为基材,对胶料性能和硫化体系、偶联剂用量进行了研究。结果表明,当镀银铝粉用量为260份,硫化体系选用DBPMH,偶联剂选用A151,硫化条件为160℃
【机 构】
：
陕西延长石油西北橡胶有限责任公司,
论文部分内容阅读
以镀银铝粉为高导电填料,硅橡胶为基材,对胶料性能和硫化体系、偶联剂用量进行了研究。结果表明,当镀银铝粉用量为260份,硫化体系选用DBPMH,偶联剂选用A151,硫化条件为160℃×15min时,所制备的镀银铝粉∕硅橡胶复合材料的综合性能较好。
Silver-plated aluminum powder as a highly conductive filler, silicone rubber as a substrate, the rubber properties and vulcanization systems, coupling agent were studied. The results show that when the amount of silvered aluminum powder is 260, DBPMH is selected as the vulcanization system, A151 is used as the coupling agent and the vulcanization condition is 160 ℃ × 15min, the prepared silver-coated aluminum powder / silicone rubber composite has better overall performance .
其他文献
研究了丙烯酸酯类助交联剂对硅橡胶硫化性能、力学性能、粘弹性能的影响。结果表明,助交联剂显著降低了硅橡胶的硫化时间、撕裂强度,明显提高了硫化胶的硬度、拉伸永久变形、
采用聚烯烃弹性体(POE)与废旧胶粉(WRP)制备了热塑性弹性体。研究了共混比、胶粉预塑炼处理工艺及白炭黑对POE/WRP力学性能的影响。结果表明,塑炼WRP/POE共混体系具有优良的
目的：探讨益气化瘀方在神经再生修复过程中对神经肌肉接头部(NMJs)生长相关蛋白-43(growth-associated protein-43，GAP-43)及蛋白基因产物9.5(Protein Gene Product 9.5，PGP9.5)
诱发电位是反映中枢神经系统功能的指标之一，应用电生理监测脊髓功能的实验和临床研究逐渐开展。本文介绍了采用电生理方法，探索脊髓慢性损伤后中枢神经诱发电位的改变，实验过程
目的：初步建立大鼠颈神经背根节(DRG)压迫模型，系统观察压迫损伤后DRG神经元病理学改变。方法：选用3月龄SPF级SD雄性大鼠20只，随机分为假手术组和压迫组，采用自制硅胶片压迫左侧C6
研究了原位生成甲基丙烯酸钠(NaMAA)和DCP对NR/BR/TPI并用胶性能的影响。结果表明,当DCP用量一定时,随着NaMAA理论生成量的增加,拉伸强度和撕裂强度先增加后减小,硬度、定伸
目的：研究正常和抗-Fas抗体诱导凋亡大鼠纤维环细胞的基因表达谱，分析抗-Fas抗体诱导凋亡大鼠纤维环细胞基因表达水平的变化。方法：建立大鼠颈椎间盘纤维环细胞培养体系，使用抗-F
广东省最近提出15条支持房企应对房市变化的意见。对在2008年签订土地出让合同、确实无法按时缴纳土地出让价款的项目用地,由土地使用者申请并经当地市、县人民政府批准,可适
以两步法工艺合成聚氨酯弹性体,通过改变多元醇、异氰酸酯种类以及扩链剂种类及配比等,考察了原料种类对聚氨酯弹性体力学性能及耐水性能的影响。结果表明,多元醇种类、异氰
目的：观察益气化瘀利水方对实验性骨关节炎兔软骨中转化生长因子-β1的影响。方法：按Colombo法建立家兔膝骨关节炎模型，将20只新西兰大白兔随机分为正常组、模型组、中药组(益气