【摘 要】
：
研究了原位生成甲基丙烯酸钠(NaMAA)和DCP对NR/BR/TPI并用胶性能的影响。结果表明,当DCP用量一定时,随着NaMAA理论生成量的增加,拉伸强度和撕裂强度先增加后减小,硬度、定伸
【机 构】
：
青岛科技大学橡塑教育部重点实验室,
论文部分内容阅读
研究了原位生成甲基丙烯酸钠(NaMAA)和DCP对NR/BR/TPI并用胶性能的影响。结果表明,当DCP用量一定时,随着NaMAA理论生成量的增加,拉伸强度和撕裂强度先增加后减小,硬度、定伸应力和拉伸永久变形增加,拉断伸长率减小;当NaMAA的理论生成量为30份时,拉伸强度和撕裂强度最好。SEM显示,NaMAA与胶料有良好的相容性,对胶料起到较好的补强作用。
The effect of NaMAA and DCP in situ on the properties of NR / BR / TPI blends was studied. The results show that when the dosage of DCP is constant, the tensile strength and tear strength first increase and then decrease with the increase of the NaMAA theoretical yield, while the hardness, tensile stress and tensile permanent set increase and the elongation at break decreases ; When the theoretical amount of NaMAA is 30, the tensile strength and tear strength are the best. SEM shows that NaMAA has good compatibility with the rubber compound and plays a good reinforcing role for the rubber compound.
其他文献
又到春暖花开时。清冷已近一年的中国地产市场在牛年春天的暖阳里开始显露复苏的迹象,并似有“重拾昨日辉煌”的气势。人春以来,关于各地房市又见活跃、成交量明显上升的信息
采用动态硫化法制备了EPDM/POE热塑性弹性体(TPV)。研究了炭黑、白炭黑和经Si-69预处理的白炭黑对TPV性能的影响。结果表明,经Si-69预处理的白炭黑补强的TPV力学性能和热性能
本研究选用27例CSM患者术中切除的椎间盘标本与16例无颈椎病史的颈椎外伤患者的颈椎间盘作为研究对象，采用放射免疫分析(RIA)法，测定其IL-6、TNF-α含量，并分析CSM组患者颈椎间
回顾上海处置在建楼房倒覆事件的得失之举,责任、法治、透明的基本理念,应是政府部门处置突发事件的出发点上海闵行区“莲花河畔景苑”小区在建楼房6月27日发生整体倒覆事件
以高乙烯基溶聚丁苯橡胶(SSBR2557A)为研究对象,研究了不同丙烯腈含量的2种丁腈橡胶(NBR1846和NBR3305)对白炭黑填充的SSBR2557A胶料加工性能、力学性能和动态性能的影响.结
研究了丙烯酸酯类助交联剂对硅橡胶硫化性能、力学性能、粘弹性能的影响。结果表明,助交联剂显著降低了硅橡胶的硫化时间、撕裂强度,明显提高了硫化胶的硬度、拉伸永久变形、
采用聚烯烃弹性体(POE)与废旧胶粉(WRP)制备了热塑性弹性体。研究了共混比、胶粉预塑炼处理工艺及白炭黑对POE/WRP力学性能的影响。结果表明,塑炼WRP/POE共混体系具有优良的
目的：探讨益气化瘀方在神经再生修复过程中对神经肌肉接头部(NMJs)生长相关蛋白-43(growth-associated protein-43，GAP-43)及蛋白基因产物9.5(Protein Gene Product 9.5，PGP9.5)
诱发电位是反映中枢神经系统功能的指标之一，应用电生理监测脊髓功能的实验和临床研究逐渐开展。本文介绍了采用电生理方法，探索脊髓慢性损伤后中枢神经诱发电位的改变，实验过程
目的：初步建立大鼠颈神经背根节(DRG)压迫模型，系统观察压迫损伤后DRG神经元病理学改变。方法：选用3月龄SPF级SD雄性大鼠20只，随机分为假手术组和压迫组，采用自制硅胶片压迫左侧C6