【摘 要】
：
A Cr-Ni type of low transformation temperature (LTT) welding filler was devised in the present study.The LTT weld microstructures of the tungsten inert gas (TIG) and metal active gas (MAG) weldings were investigated by using electron-backscattered diffrac
【机 构】
：
School of Materials Science and Engineering, Tianjin University, No.135 Yaguan Road, Jinnan District
论文部分内容阅读
A Cr-Ni type of low transformation temperature (LTT) welding filler was devised in the present study.The LTT weld microstructures of the tungsten inert gas (TIG) and metal active gas (MAG) weldings were investigated by using electron-backscattered diffraction and orientation imaging microscopy.The results showed that the LTT weld microstructures prepared by TIG and MAG weldings were primarily martensite with 17.5％ and 8.0％ retained austenite,respectively.The LTT weld metal using TIG welding had larger grain size than using MAG.In addition,based on the Taylor factor calculation,the weld metal using MAG welding was more competent in repressing fatigue crack initiation.Meanwhile,the high angle and coincidence site lattice grain boundaries were dominant in the LTT weld metal using MAG welding.Moreover,the hardness of the LTT weld metal using MAG welding was higher than that of using TIG.Based on heat input and phase transformation,finite element method was applied to analyzing the tensile residual stress (RS) reduction in welded joints prepared by both conventional and LTT welding fillers,respectively.The corresponding outcome confirmed that the LTT weld metal using MAG welding was more beneficial to tensile RS reduction.
其他文献
Pure tetragonal 10-20-nm-size zirconia-based Ni-P composite coating was developed.The physicochemical and electrochemical characteristics including corrosion resistance of the coating were investigated.The Ni-P-nano-tetragonal zirconia coating was partial
The gradient mechanical properties,variation of stress with strain and surface cracking behavior of expanded austenite developed on 316L austenitic stainless steel were investigated by nanoindentation tests,X-ray residual stress analysis and scanning elec
A facile scalable synthesis of hierarchical Sb/C micro-/nanohybrid has been addressed in this work, which possesses the advantages of both micrometer and nanometer scale structures as lithium-ion battery anode. Difunctional methacrylate monomers are used
Ternary Zn-0.5Al-0.5Mg and quaternary Zn-0.5Al-0.5Mg-xBi (x =0.1,0.3 and 0.5) alloys were studied to evaluate the thermal and structural characteristics,mechanical properties,cytotoxicity and in vitro degradation behavior.Thermal analysis and microstructu
The present work investigates how axial static magnetic field affects the solidification structure and the solute distribution in directionally solidified GCrl8Mo steel.Experimental results show that grain refinement and the columnar to equiaxed transitio
In this study,the dissimilar friction stir welding (FSW) butt joints between aluminum alloy 5754-H114 and commercially pure copper were investigated.The thickness of welded plates was 4 mm and the aluminum plate was placed on the advancing side.In order t
The effects of electropulsing-assisted ultrasonic surface rolling process on surface mechanical properties and microstructure evolution of commercial pure titanium were investigated.It was found that the surface mechanical properties were significantly en
Continuous solidification experiments are carried out with Pb-Al alloys under the influence of the electric current pulses (ECPs).The results demonstrate that the ECPs mainly affect the microstructure formation through changing the energy barrier for the
Effect of trace O element on the high-temperature wettability between Ni3Al scrap melt and Y2O3 ceramic at 1873 K is investigated.With the increase in O content in Ni3Al scrap melt from 6 to 21 ppm,the equilibrium contact angledecreases from 93.3° to 88.9