In this study,the dissimilar friction stir welding (FSW) butt joints between aluminum alloy 5754-H114 and commercially pure copper were investigated.The thickness of welded plates was 4 mm and the aluminum plate was placed on the advancing side.In order t
【机 构】
：
Department of Mining and Metallurgical Engineering,Amirkabir University of Technology, Tehran, Iran
论文部分内容阅读
In this study,the dissimilar friction stir welding (FSW) butt joints between aluminum alloy 5754-H114 and commercially pure copper were investigated.The thickness of welded plates was 4 mm and the aluminum plate was placed on the advancing side.In order to obtain a suitable flow and a better material mixing,a 1-mm offset was considered for the aluminum plate,toward the butt centerline.For investigating the microstructure and mechanical properties of FSWed joints,optical microscopy and mechanical tests (i.e.,uniaxial tensile test and microhardness) were used,respectively.Furthermore,the analysis of intermetallic compounds and fracture surface was examined by scanning electron microscopy and X-ray diffraction.The effect of heat generation on the mechanical properties and microstructure of the FSWed joints was investigated.The results showed that there is an optimum amount of heat input.The intermetallic compounds formed in FSWed joints were Al4Cu9 and Al2Cu.The best results were found in joints with 1000 rpm rotational speed and 100 mm/min travel speed.The tensile strength was found as 219 MPa,which reached 84％ of the aluminum base strength.Moreover,maximum value of the microhardness of the stir zone (SZ) was attained as about 120 HV,which was greatly depended on the grain size,intermetallic compounds and copper pieces in SZ.
其他文献
The GH4169 superalloy with different content of δ-Ni3Nb phase was welded by tungsten inert gas welding.A detailed study of microstructure and hardness of heat-affected zone (HAZ) was performed in both as-welded and aged state.The results show that the pre
Experiments were carried out to investigate the corrosion behavior of epoxy-coated rebar (ECR) with pinhole defect (diameter in hundreds of microns) immersed in the uncarbonated/carbonated simulated pore solution (SPS) of seawater concrete.Corrosion behav
By using a novel surface modification technique named ultrasonic-electropulsing coupling rolling (UECR) process on an A1-Si casting alloy rod,the surface of material was smoothened significantly.Meanwhile,a strengthened layer with a gradient change in har
This paper reports TiC-(Ni-Cr) metal ceramic alloy (ratio of components 50∶50) with nanoscaled components formed in the surface layer and smoothly transformed into the initial inner structure throughout the material under pulsed electron irradiation of th
In this work,(1-x)CdO-xSnO2 nanocomposites (≤ 0.15) have been synthesized via hydrothermal route.The structural study reveals that CdO nanostructures possess crystalline phase and cubic structure.The CdO-SnO2 nanocomposites possess both cubic and orthorho
Pure tetragonal 10-20-nm-size zirconia-based Ni-P composite coating was developed.The physicochemical and electrochemical characteristics including corrosion resistance of the coating were investigated.The Ni-P-nano-tetragonal zirconia coating was partial
The gradient mechanical properties,variation of stress with strain and surface cracking behavior of expanded austenite developed on 316L austenitic stainless steel were investigated by nanoindentation tests,X-ray residual stress analysis and scanning elec
A facile scalable synthesis of hierarchical Sb/C micro-/nanohybrid has been addressed in this work, which possesses the advantages of both micrometer and nanometer scale structures as lithium-ion battery anode. Difunctional methacrylate monomers are used
Ternary Zn-0.5Al-0.5Mg and quaternary Zn-0.5Al-0.5Mg-xBi (x =0.1,0.3 and 0.5) alloys were studied to evaluate the thermal and structural characteristics,mechanical properties,cytotoxicity and in vitro degradation behavior.Thermal analysis and microstructu
The present work investigates how axial static magnetic field affects the solidification structure and the solute distribution in directionally solidified GCrl8Mo steel.Experimental results show that grain refinement and the columnar to equiaxed transitio