The nanocomposite films were prepared by direct intercalation of poly(ethylene oxide) and PEO into MoO 3 xerogel via sol-gel route.The electrochromic behavior and the chemical conditions of Li + ions were investigated by cyclic voltammograms,UV-visible spectral transmittance and XPS.The results show that the cycling efficiency and the reversibility of insertion/extraction of Li + ions in (PEO) 1MoO 3·nH 2O nanocomposite film were improved.The intercalation of PEO into MoO 3 xerogel modulated the wavelength range of electrochromism and enhanced the electrochromic efficiency.Two different chemical conditions of Li + ions existing in the interlayer and interstitial positions of MoO 3 lattice were observed in MoO 3 xerogel and (PEO) 1MoO 3·nH 2O nanocomposite films.
The nanocomposite films were prepared by direct intercalation of poly (ethylene oxide) and PEO into MoO 3 xerogel via sol-gel route. The electrochromic behavior and the chemical conditions of Li + ions were investigated by cyclic voltammograms, UV-visible spectral transmittance and XPS . The results show that the cycling efficiency and the reversibility of insertion / extraction of Li + ions in (PEO) 1MoO 3 · nH 2O nanocomposite film were improved.The intercalation of PEO into MoO 3 xerogel modulated the wavelength range of electrochromism and enhanced the electrochromic efficiency. Two different chemical conditions of Li + ions existing in the interlayer and interstitial positions of MoO 3 lattice were observed in MoO 3 xerogel and (PEO) 1MoO 3 · nH 2O nanocomposite films.