【摘 要】
：
A modified strain-induced melt activation (SIMA) process consisting of homogenization,equal-channel angular pressing (ECAP) and subsequent heating to the semisolid temperatures was introduced to prepare the 7075 aluminum alloy with superior thixotropic be
【机 构】
：
School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 1
论文部分内容阅读
A modified strain-induced melt activation (SIMA) process consisting of homogenization,equal-channel angular pressing (ECAP) and subsequent heating to the semisolid temperatures was introduced to prepare the 7075 aluminum alloy with superior thixotropic behaviors.The effects of both the homogenization and the number of ECAP passes,as well as the isothermal temperatures on the microstructural evolution,were investigated.The results indicate that ideal microstructure wherein fine and globular solid grains surrounded by uniform liquid films can be achieved through ECAP deformation-recrystallization mechanism.Increasing the number of ECAP passes accelerates the recrystallization of strained grains,thus reducing the average grain size and improving the grain sphericity.Moreover,higher holding temperatures and prolonged soaking time can improve the growth of the solid grains.Two main coarsening mechanisms,viz.coalescence and Ostwald ripening,contribute to the growth of the solid grains simultaneously and independently.The tensile strength of the 7075 alloys after four-pass ECAP-based SIMA and T6 heat treatment is relatively lower than the as-received billet,while the elongation of SIMA processed samples is much higher than that of as-received ones.Increasing the number of ECAP passes improves the tensile strength for alloys with and without T6 treatment due to the fine grain strengthening mechanism.
其他文献
Particle reinforced magnesium matrix composite (PMMC) possesses the merits of high specific strength,high specific modulus,better dimensional stability,good wear resistance and lower production cost,which is thought as a promising material in the field of
Novel crystallization behaviors of Zr55Cu30Al1oNi5 bulk metallic glass are investigated.On the one hand,mixed oxides,including CuO,CuAlO2,CuAl2O4 and ZrO2,show sequential oxidation process determined by coupling effects of specific cyclic load and tempera
The defects created in commercial dental alloys during blasting with alumina particles propelled in compressed air under pressure 0.1 and 0.4 MPa have been studied using positron annihilation spectroscopy,scanning electron microscopy and X-ray diffraction
A series of Ti2ZrHf0.5VNbx (x =0,0.25,0.5,0.75 and 1.0) refractory high-entropy alloys were prepared to investigate the alloying effect of Nb on the microstructures and mechanical properties.All the alloys displayed a simple BCC structure.The microstructu
The development of high-entropy alloys (HEAs) has stimulated an ever-increasing interest from both academia and industries.In this work,three novel MoNbFeCrV,MoNbFeCrTi,and MoNbFeVTi HEAs containing low thermal neutron absorption cross section elements we
This paper presents a new thermomechanical model of friction stir welding which is capable of simulating the three major steps of friction stir welding (FSW) process,i.e.,plunge,dwell,and travel stages.A rate-dependent JohnsonCook constitutive model is ch
A calculation method based on a combination of △g parallelism rule,good matching site (GMS) analysis,CSL/DSCL (coincidence site lattice/displacement shift complete lattice) and the O-lattice theory has been applied to interpret the observation of the habi
In pressurized water reactor,fretting corrosion has become the main reason for the failure of 690TT heat exchanger tubes.The effect of temperature on the fretting corrosion behavior between 690TT tube and 405 stainless steel (SS) bar has been studied duri
Mg-3Al-1Zn alloy sheets have been deformed by continuous bending (CB) to investigate the effects of processing parameters (bending angle and repetitive passes) on the texture and formability.The samples exhibited a bimodal microstructure with abnormal gro
The microstructure,texture,residual stress,and tensile properties of Mg-6Zn-2Y-1La-0.5Zr (wt％) magnesium alloy were investigated before and after extrusion process,which performed at 300 ℃ and 400 ℃.The microstructural characterizations indicated that the