【摘 要】
：
Microbial corrosion is a major corrosion related problem for steel pipelines.There is an urgent need for oil industry to develop environmentally friendly strategies for microbial corrosion control.
【机 构】
：
Institute of Metal Research,Chinese Academy of Sciences,72 Wenhua Road,Shenyang 110016,PR China;Univ
【出 处】
：
国际腐蚀工程大会(ICEC2016)
论文部分内容阅读
Microbial corrosion is a major corrosion related problem for steel pipelines.There is an urgent need for oil industry to develop environmentally friendly strategies for microbial corrosion control.
其他文献
Certain species of sulfate-reducing bacteria(SRB)use cathodes as electron donors for metabolism,and this electron transfer process may influence the proper protection potential choice for structures.
Surface and interfacial chemistry plays a critical role in developing advanced anti-corrosion systems,and the key to the successful coating system is the initial formation of a chemical conversion fil
The microbiologically influenced corrosion was investigated in the early failed copper pipes by pitting used in underground water.The bacteria were cultured by sampling from corrosion product near pit
In this work,the passivation behavior and galvanic corrosion of 304 stainless steel elbow under erosion-corrosion(E-C)condition were studied by array electrodes technique through a loop system.
The corrosion behavior and mechanism of under deposit corrosion of ammonium chloride salt of 10# carbon steel under various temperatures and relative humidity were investigated by the weight loss meth
With wide application of electronic products,they are becoming an indispensable part of our life.The service life of electronic components is attracting more and more attention.
Stress corrosion cracking(SCC)is a common type of equipment failure in chemical industry,especially for stainless steels equipment.However,many end users are not familiar with this failure mode when i
Biocorrosion,also known as microbiologically influenced corrosion(MIC),is a major problem in the oil and gas industry as well as many other industrial sectors.
The failure of an air preheater is investigated in this paper.Deposit samples and corroded heating elements were taken from the air preheater of a 300MW coal-fired power plant in Wuhan Province,China,
In a static environment,based on the heat erosion test by immersing in molten salt and electrochemical test of the heat erosion of the molten salt,the corrosion properties of the 316L,321H,P91,12CrMoV