SRB induced accelerated corrosion attack of high strength steel under-0.85 VSCE cathodic polarizatio

来源 :国际腐蚀工程大会(ICEC2016) | 被引量 : 0次 | 上传用户：marine_ogz

【摘要】

：

Certain species of sulfate-reducing bacteria(SRB)use cathodes as electron donors for metabolism,and this electron transfer process may influence the proper protection potential choice for structures.

【作者】

：

Fang Guan Jizhou Duan Xiaofan Zhai Baorong Hou

【机构】

：

Marine Corrosion and Protection Centre,Institute of Oceanology,Chinese Academy of Sciences,No.7 Nanh

【出处】

：

国际腐蚀工程大会(ICEC2016)

【发表日期】

：

2016年10期

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　Certain species of sulfate-reducing bacteria(SRB)use cathodes as electron donors for metabolism,and this electron transfer process may influence the proper protection potential choice for structures.

其他文献

Equivalent Degradation of Aviation Organic Coating during In-door Accelerated Testing and Outdoor Ex

The relationship between indoor accelerated testing and outdoor exposure in terms of equivalent degradation in aviation organic coating was studied in order to provide fundamental data for the life pr

会议

Use of Facile Color-change Indicators to Quantify Passive Films on Stainless Steel Facilities of Nuc

The inspection of passive film quality on stainless steel facilities is a key process during the construction engineering of nuclear power plants,but the traditional blue dot method might pose health

会议

Investigation on the corrosion resistance of materials for expander's impeller

FV520B steel,17-4PH steel and Inconel 718 alloy are investigated as the proper used materials for the impeller of the expander in this work.The general corrosion and pitting corrosion properties of th

会议

Laboratory Investigation of Microbiologically Influenced Corrosion(MIC)Resistance of a Novel Cu-bear

The microbiologically influenced corrosion(MIC)resistance of a novel Cu-bearing 2205 duplex stainless steel(2205-Cu DSS)against an aerobic marine Pseudomonas aeruginosa biofilm was investigated.

会议

Revealing Blister Formation Process on Aluminum Surface in Hydrogen Environment

The corrosion resistance of metals relies on a passivating surface layer of dense and adherent oxide.However,the integrity of such a protective oxide is compromised in the presence of excess hydrogen

会议

Corrosion of The stainless clad steel with AC interference in concrete

The research of different gradient AC interference on corrosion rule of The 304 stainless clad steel was studied by polarization curve experiment in concrete.Results indicate that alternating current

会议

Electrodeposting Al-Mn coating on mild steel screws and its corrosion behavior

In this paper we show that screws made of mild steel can,in principle,be electrochemically coated with up to 20-μm-thick amorphous Al-Mn coatings in an ionic liquid composed of MnCl2-AlCl3-1-ethyl-3-m

会议

Materials Science Journals in IMR

Six science journals are published in the Institute of Metal Reasarch,Chinese Academy of Sciences(IMRCAS).In this reports,we introduce the history and current development of these journals in IMR,putt

会议

An Engineering Case According to the Application of Sea Sand in Reinforced Concrete

1.Engineering application environment: Sanshan island which located in the South Bank of Bohai Bay(Shandong),is a small peninsula surrounded by water on three sides.

会议

Sulfate-reducing bacteria induced the localized corrosion of Q235 steel

Localized corrosion behavior of Q235 steel in seawater containing sulphate-reducing bacteria(SRB)is investigated by wire beam electrode(WBE)technique,electrochemical measurement method and surface ana

会议

SRB induced accelerated corrosion attack of high strength steel under-0.85 VSCE cathodic polarizatio

其他学术论文