High-cycle fatigue life prediction of AZ31B magnesium alloy welding joints through infrared thermogr

来源 :2013年国际焊接结构疲劳断裂学术会议 | 被引量 : 0次 | 上传用户：ruiping009

【摘要】

：

This paper presents an experimental approach to predict fatigue life ofAZ31B magnesium alloy butt joints based on infrared thermography.The thermographic technique is used to monitor the temperature e

【作者】

：

Liu Xiao-Qing Zhang Hong-Xia Yan Zhi-Feng Zhou Ya-Guo Zhang Qian-Ming Wang Wen-Xian

【机构】

：

College of Material Science and Engineering,Taiyuan University of Technology,Taiyuan 030024

【出处】

：

2013年国际焊接结构疲劳断裂学术会议

【发表日期】

：

2013年1期

【关键词】

：

AZ31B magnesium alloy butt joint high-cycle fatigue life infrared thermography

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

轮对服役因素对高速列车振动性能的影响

轮对型面磨耗严重影响高速列车服役振动性能，型面曲线的微小改变会引起轮轨接触性能的大幅下降，若同时考虑轮对柔性对振动的传递作用，相比轮对刚性时，构架及车体的振动加速度会发生较大变化，本文从轮对型面磨耗及其柔性入手考虑轮对服役因素对高速列车振动性能的影响。

会议

高速列车服役性能轮对磨耗轮对柔性振动加速度频谱分析

Mechanical properties of pinless friction stir welding of 2024 aluminum alloy

Joining the thin sheet aluminum alloys(<2.0 mm)are difficult via conventional friction stir welding owing to the root flaw and keyhole.In the present research,a newly designed pinless tool with involu

会议

Pinless FSW2024 aluminium alloysmechanical properties

Prediction of SCC in the heat affected zone in core shroud of boiling water reactor

Stress corrosion cracking(SCC)in the welded joint of a core shroud is the primary damage due to weld residual stress,corrosion and neutron irradiation environment in a boiling water reactor.The predic

会议

Core shroud316L stainless steelweld residual stressnumerical simulationSCC p

平行等长度表面裂纹应力强度因子复合原则

大型化工容器中存在大量的焊缝，在焊接残余应力及腐蚀介质的联合作用下，易产生垂直于焊缝的应力腐蚀裂纹，这些裂纹相互平行，且排列密集，裂纹尖端应力之间可能出现相互干涉问题，因而有必要对该类裂纹的应力强度因子复合问题进行研究，本文采用断裂力学的方法考虑平行裂纹间的相互影响，以确定合适的裂纹复合模型。

会议

应力强度因子复合裂纹平行裂纹断裂力学

Microstructure and fatigue performance of electron beam welded joints of AZ31B magnesium ahoy

10 mm thick AZ31B magnesium alloy plate was welded by the electron beam welding(EBW).The microstructure,elements distribution,tensile mechanical properties and fatigue behavior of EBW joint were measu

会议

Electron beam weldingAZ31B magnesium alloyfatigue fracturecrack propagationm

The thermodynamic behavior of AZ31B magnesium alloy under tensile and cyclic loading

Temperature evolution of AZ31B magnesium alloy plate was measured under static and cyclic loading by the approach of infrared thermograph.The mechanism of heat generation under different load level wa

会议

AZ31B alloyinfrared thermographmechanism of heat generation

Statistical analysis on probability characteristic of fatigue crack growth rate

The standard center-cracked tensile specimens M(T)with different widths made of aluminum alloy from high-speed train were designed for fatigue crack propagation rate testing.

会议

Fatigue crack growth rateprobability characteristicstatistical analysis

Rapid determination for fatigue parameters of AZ31B basing on temperature evolution under HCF

An experiment study was carried out to investigate the temperature field evolution of the extruded AZ31B magnesium alloy specimens under high cyclic fatigue(HCF)load basing on infrared thermographic m

会议

Infrared thermographyenergy approachfatigue strengthresidual fatigue lifeS-N

Fatigue life prediction of elastic stitched catenary based on nominal stress method

As the speed of high-speed trains on electrified railways is continually increasing,malfunctions happened occasionally such as broken line accident.

会议

Catenaryfatigue Lifecontact Linehigh-speed railway

Research on fatigue behavior of AZ31B magnesium alloy butt welded joint based on infrared thermograp

The fatigue behavior of AZ31B magnesium alloy butt welded joint during high cycles fatigue testing was investigated by infrared thermography.

会议

AZ31B magnesium alloywelded jointfatigueinfrared thermograhyweld reinforceme

High-cycle fatigue life prediction of AZ31B magnesium alloy welding joints through infrared thermogr

其他学术论文