In this study, wood-plastic plywood was fabricated with high density polyethylene (HDPE) film and poplar veneer by hot-pressing.To improve the interfacial a
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
In this study, wood-plastic plywood was fabricated with high density polyethylene (HDPE) film and poplar veneer by hot-pressing.To improve the interfacial adhesion between the wood veneer and HDPE film, poplar veneers were treated in the oven under different temperatures (130, 160, 180, 200 ℃) before they were composited with HDPE film.
其他文献
With the increasing pressure on the world's resources as well as concerns about the disposal of materials, biodegradable materials have received lots of res
This study investigated the influence of wood fiber and two common lubricants on the rheological behavior of wood fiber/polypropylene composites.The results
Nanocellulose and chitosan are both natural biological polysaccharides, and their combination composites can improve performance and enlarge application fie
Natural chitosan (CS) at four different additions (10, 20, 30 and 40 phr) and particle size ranges (100-140, 140-180, 180-220, and over 260 mesh) are select
In this study, four kinds of natural fibers which were extracted from different plant sources were investigated.The microstructures of these natural fibers
Commercial wood-plastic composite (WPC) floor have shortcomings of bad surface decoration effect.Through the surface painting to improve the surface effect,
Effects of processing temperature on both static and dynamic mechanicalproperties of flax fiber reinforced composites (FFRC) were investigated.Initially, th
Wood flour (WF) used as reinforcement in thermoplastics are popular, but the poor compatibility between WF and polymer matrix and relative high moisture abs
Unidirectional flax fiber reinforced epoxy composites (FFRC) were fabricated using a hot pressing process.The effect of stacking sequence on the impact and
Rice straw, wheat straw, wood flour were used to mix with melt high density polyethylene (HDPE) through an extruder to prepare natural fiber/HDPE composites