【摘 要】
：
The use of niobium as a microalloying element in high strength steels is now well-known and widely adopted.However,with recent advances in thermo-mechanical processing,inclusive of ultrafast cooling t
【机 构】
：
Department of Metallurgical and Materials Engineering,University of Texas at El Paso 500 W. Universi
论文部分内容阅读
The use of niobium as a microalloying element in high strength steels is now well-known and widely adopted.However,with recent advances in thermo-mechanical processing,inclusive of ultrafast cooling technology,and modifications in alloy design,niobium continues to provide significant mechanical property and processing benefits.With this in perspective,we describe here the footprint of niobium in the new generation of high strength microalloyed steels that involve low carbon-based alloy design approach.In this regard,we underscore the effectiveness of niobium in low carbon-Nb(or low C-Nb-Ti)microalloyed steels in terms of obtaining superior mechanical properties and cost-effectiveness,using recent experiences in the processing of microalloyed steels.Also,elucidated are precipitation and microstructural characteristics when niobium is used as a standalone microalloying element or in conjunction with titanium and molybdenum.
其他文献
Effect of a high magnetic field of 8T on the pearlite transformation was investigated in a Fe-0.4mass%C steel.It was found that a magnetic field of 8T can promote the pearlite transformation,reduce th
盾构隧道在运营过程中由于种种原因发生过量的纵向沉降或不均匀沉降,引发隧道渗水漏泥、结构局部破坏,或内部结构(如地铁轨道)发生纵向扭曲变形,而影响隧道的正常运营.目前,很多隧道加固研究是加固隧道断面,只有较少学者对隧道纵向进行过加固研究,本文采用CFRP网格加固盾构隧道进行缩尺模型试验.试验结果表明,盾构隧道纵向等效抗弯刚度有效提高,达到加固补强的作用.
Multi-pass deformation simulation tests were performed on V-N microalloyed steels with different nitrogen addition by using a Gleeble-3800 thermo-mechanical simulator and the corresponding continuous
Instead of off-line quenching and tempering(QT),on-line ausforming(non-recrystallization controlled roling)and direct quenching(DQ)was employed to improve the toughness of low alloy steel with yield s
A cost effective alloy design based on niobium microalloying was developed by Shagang for the production of 32 mm gage K60-E2 steel plate for manufacturing LSAW pipes of 1422 mm diameter.Two metallurg
The effect of Mo addition on the precipitation of carbides both in austenite and ferrite of Nbbearing HSLA steel were investigated by stress relaxation and transmission electron microscopy(TEM).Experi
International Standard ISO 6892-2 maintains that strain rate variations can induce the measurement uncertainty of mechanical properties in tensile testing,which will imperil the reliability of tension
The microstructure,mechanical property and precipitation behavior in a low carbon Nb-Ti micro-alloyed steel were investigated using dilatometer,optical microscopy and transmission electron microscope.
The influence of Nb,Mo,Cr and B on phase transformations and mechanical properties are studied in a 0.15C-2.0Mn-0.3Si-0.020Ti dual phase steel separately and in combination.The formation and decomposi
Deformation processes of microalloyed steels,both during hot and cold processing,are characterized by complex interactions between fine strain-induced precipitates and deformation activated movement o