The microstructure,mechanical property and precipitation behavior in a low carbon Nb-Ti micro-alloyed steel were investigated using dilatometer,optical microscopy and transmission electron microscope.
【机 构】
：
State Key Laboratory of Rolling and Automation,Northeastern University,Shenyang 110819,China
论文部分内容阅读
The microstructure,mechanical property and precipitation behavior in a low carbon Nb-Ti micro-alloyed steel were investigated using dilatometer,optical microscopy and transmission electron microscope.The results show that the microstructure of the experimental steel treated by isothermal quenching process mainly consists of ferrite and martensite.The volume fraction of ferrite increases with a decrease in the isothermal temperature.It is found that both of interphase precipitation and supersaturated precipitation would appear in the samples treated by isothermal quenching process.Along with the isothermal temperature decreasing,the precipitation state changes from interphase precipitation to supersaturated precipitation.The interphase precipitation of these carbides with different row spacing and different orientation in ferrite grains,is related to the mobility of interfaces during/transformation based on ledge mechanism.In addition to {110} plane suggested by the ledge mechanism,the planar sheets of interphase precipitation are also found to be parallel with{035} planes.Moreover,the interphase precipitation carbides were identified to have a NaCl-type crystal structure with a lattice parameter of 0.432 nm and obey the Baker–Nutting(B–N)orientation relationship with respect to ferrite matrix.The contribution of the precipitation hardening to the yield strength of the experiment steel has been estimated to be~337 MPa at 620℃,based on Orowan mechanism.
其他文献
采用外贴FRP或附加粘滞阻尼器方式对钢筋混凝土框架结构进行加固,可有效改善结构的抗震性能.为比较分析两种加固形式及不同加固方案对多层钢筋混凝土框架结构抗震性能的影响,本文基于OpenSees有限元分析平台,对FRP或附加粘滞阻尼器加固前后的多层钢筋混凝土框架结构模型进行了弹塑性动力时程反应分析.分析结果表明:FRP加固后提高了结构的变形及抗震能力,但并不能减小结构的位移响应,而采用粘滞阻尼器加固则
在上世纪80年代前后,我国建成了较多的钢筋混凝土T梁桥,这类T梁桥经过多年的营运,已经出现了较多的病害,其加固方法值得研究.本文以一座20米钢筋混凝土T梁桥的加固设计为基础,进行了多个加固方案的对比,计算表明,采用预应力碳纤维板和增厚翼板的组合加固法,不但可以大幅度提高T梁的承载力能力,而且加大的预应力碳纤维,可以提供更多的预拉力,改善T梁的使用性能;此外增厚的翼板混凝土与其它T梁横向联系加固措施
Decomposition of supercooled austenite in continuous cooling transformation process of a Mn-Mo-Ni low alloy steel was evaluated by dilatometric measurements,light microscopy,electron backscatter diffr
Effect of a high magnetic field of 8T on the pearlite transformation was investigated in a Fe-0.4mass%C steel.It was found that a magnetic field of 8T can promote the pearlite transformation,reduce th
盾构隧道在运营过程中由于种种原因发生过量的纵向沉降或不均匀沉降,引发隧道渗水漏泥、结构局部破坏,或内部结构(如地铁轨道)发生纵向扭曲变形,而影响隧道的正常运营.目前,很多隧道加固研究是加固隧道断面,只有较少学者对隧道纵向进行过加固研究,本文采用CFRP网格加固盾构隧道进行缩尺模型试验.试验结果表明,盾构隧道纵向等效抗弯刚度有效提高,达到加固补强的作用.
Multi-pass deformation simulation tests were performed on V-N microalloyed steels with different nitrogen addition by using a Gleeble-3800 thermo-mechanical simulator and the corresponding continuous
Instead of off-line quenching and tempering(QT),on-line ausforming(non-recrystallization controlled roling)and direct quenching(DQ)was employed to improve the toughness of low alloy steel with yield s
A cost effective alloy design based on niobium microalloying was developed by Shagang for the production of 32 mm gage K60-E2 steel plate for manufacturing LSAW pipes of 1422 mm diameter.Two metallurg
The effect of Mo addition on the precipitation of carbides both in austenite and ferrite of Nbbearing HSLA steel were investigated by stress relaxation and transmission electron microscopy(TEM).Experi
International Standard ISO 6892-2 maintains that strain rate variations can induce the measurement uncertainty of mechanical properties in tensile testing,which will imperil the reliability of tension