【摘 要】
：
Ni-Co-Fe-P quaternary alloy coatings were electrodeposited and the dependence of microstructure and erosion-corrosion resistance with varying P content was investigated.With the addition of H3PO3 from
【机 构】
：
College of Mechanical & Electrical Engineering,Hohai University,Changzhou 213022,China
【出 处】
：
国际腐蚀工程大会(ICEC2016)
论文部分内容阅读
Ni-Co-Fe-P quaternary alloy coatings were electrodeposited and the dependence of microstructure and erosion-corrosion resistance with varying P content was investigated.With the addition of H3PO3 from 0 to 40 g L-1 into the electrolyte bath,the P content in Ni-Co-Fe-P quaternary alloy coating was increased to 12.92 wt.%.
其他文献
The failure of an air preheater is investigated in this paper.Deposit samples and corroded heating elements were taken from the air preheater of a 300MW coal-fired power plant in Wuhan Province,China,
In a static environment,based on the heat erosion test by immersing in molten salt and electrochemical test of the heat erosion of the molten salt,the corrosion properties of the 316L,321H,P91,12CrMoV
Microbial corrosion is a major corrosion related problem for steel pipelines.There is an urgent need for oil industry to develop environmentally friendly strategies for microbial corrosion control.
Metallic oxide(scale)inevitably generates on the surface of steel strip due to thermal oxidation at elevated temperatures in corrosive environments.This sort of oxide scale can therefore cause the sur
The effect of H2S content on corrosion behavior of X70 pipeline steels in water-unsaturated(2500 ppmv)supercritical CO2 system containing 1000 ppmv O2 was investigated by means of weight loss tests,SE
According to the research project from Power China,which is named “Protection measures and application study for offshore wind energy engineering”,requirements for offshore wind energy protective coat
There is currently significant interest in titanium alloys for downhole tubulars and components for corrosive oil and gas wells due to their combination of strength,density and corrosion resistance.
Hastelloy C-276 alloy is a Ni-Cr-Mo-W wrought alloy that has good high temperature strength,resistance to neutron radiation,and perfect anti-oxidation abilities.Through small amount of deformation by
The tensile properties and fracture behaviors of a low alloy steel subjected to various tempering temperature conditions(25℃,200℃,400℃ and 650℃ respectively)after hydrogen charging were investigated b
The LPR technique is commonly used to measure corrosion rates,both in labs and in the field,but the widespread application of this electrochemical technique does not mean that it is without complicati