【摘 要】
：
Using slag, steel slag and Portland cement as the raw material with a small amount of activator, the composite Portland cement of magnitude 42.5R was prepared.The steel slag fineness, the composite ra
【机 构】
：
School of Materials science and Engineering, Shenyang Jianzhu University, No.9 Hunnan East Road Hunn
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
Using slag, steel slag and Portland cement as the raw material with a small amount of activator, the composite Portland cement of magnitude 42.5R was prepared.The steel slag fineness, the composite ratio of slag-steel slag and the types of activator on the properties of composite Portland cement were studied in the research.The hydrated products of composite Portland cement and the micro-structure of harden cement paste were analyzed by SEM.The results show that the greater the specific surface area of steel slag is, the shorter the setting time, and the higher the mortar strength will be.The cement setting time is prolonged, the expansion rate is increased and the mortar strength is decreased with the increase of the percentage of steel slag in composite Portland cement.The activity of slag and steel-slag is increased, the setting time is shortened and the mortar strength of each age is significantly increased with the adding of alkaline activator to composite Portland cement.Besides, SEM photos show that adding sodium silicate makes the cement hydration accelerated, C-S-H gel and ettringite crystal continuously formed, the bonding degree of cement and aggregate increased, the gap of cement paste decreased and filled with hydration products.
其他文献
This study investigates the sulfate resistance of binary, ternary and quaternary mixes of Portland clinker,calcareous fly ash, slag and limestone.Neat and limestone cements expanded to damage within l
Shrinkage reducing admixtures (SRAs) can alter ionic movement in concrete by changing the properties of pore fluid.This study examines the influence of SRA on chloride binding and diffusion.SRA was fo
In this paper, the zeta potential of freshly mixed cement paste and hardened cement pastes, as well as the concentration index, was measured.The influences of chloride concentration in mixing water an
Chloride-induced corrosion is one of the main causes of reinforced-concrete structure degradation.Chloride ingress is delayed by the interactions between chlorides and the cementitious matrix.In this
In this study we report on the durability of newly developed cement-reduced eco-friendly concretes with high limestone powder content and low water-powder ratios against sulfate attack.This study pres
X-ray tomography (X-CT) was applied to track in-situ, continuously and visually the migration process of water in unsaturated cement pastes.The effects of water to cement ratio were investigated.Accor
The degradation of sulphoaluminate cement (SAC) subjected to wet-dry cycles in sulfate solution was studied in this paper.The surface corrosion was recorded and the microstructures were examined by sc
Cyclic freeze-thaw has been recognized as one of the most primary factors leading to structure and function failure of concrete.Strain, which may have certain inherent advantages compared to tradition
During the hydration of cement tricalcium aluminate (C3A) reacts with gypsum and forms Ettringite (AFt).Once all gypsum is consumed ettringite can further react with remaining C3A and form monosulfate
The effect of dolomite on alite hydration was investigated in order to elucidate the effect of dolomite addition in cement hydration.The rate of heat evolution both in cement-dolomite and alite-dolomi