【摘 要】
：
The effect of dolomite on alite hydration was investigated in order to elucidate the effect of dolomite addition in cement hydration.The rate of heat evolution both in cement-dolomite and alite-dolomi
【机 构】
：
University of Science and Technology AGH, Kraków 30-059, al.Mickiewicza 30 Poland
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
The effect of dolomite on alite hydration was investigated in order to elucidate the effect of dolomite addition in cement hydration.The rate of heat evolution both in cement-dolomite and alite-dolomite system was taken as a starting point.Subsequently the chemical shrinkage, conductivity of liquid phase and rheological parameters of pastes were characterized.The observations of microstructure were carried out under SEM and the hydration degree of alite was determined by XRD.The accelerating effect of additive was proved.At low percentage dolomite plays a role of cement replacement;at higher dosage-the ,,dilution" effect can be observed.However,increasing dolomite content is accompanied by higher amount of hydration products, as a results of crystallization on the fine dolomite grains and better absorption of water.The hydration degree of alite increases as well.
其他文献
In this paper, the distributions and relationships among total, bound and free chloride ions in different forms in the concrete with different supplementary cementitious materials at different curing
This study investigates the sulfate resistance of binary, ternary and quaternary mixes of Portland clinker,calcareous fly ash, slag and limestone.Neat and limestone cements expanded to damage within l
Shrinkage reducing admixtures (SRAs) can alter ionic movement in concrete by changing the properties of pore fluid.This study examines the influence of SRA on chloride binding and diffusion.SRA was fo
In this paper, the zeta potential of freshly mixed cement paste and hardened cement pastes, as well as the concentration index, was measured.The influences of chloride concentration in mixing water an
Chloride-induced corrosion is one of the main causes of reinforced-concrete structure degradation.Chloride ingress is delayed by the interactions between chlorides and the cementitious matrix.In this
In this study we report on the durability of newly developed cement-reduced eco-friendly concretes with high limestone powder content and low water-powder ratios against sulfate attack.This study pres
X-ray tomography (X-CT) was applied to track in-situ, continuously and visually the migration process of water in unsaturated cement pastes.The effects of water to cement ratio were investigated.Accor
The degradation of sulphoaluminate cement (SAC) subjected to wet-dry cycles in sulfate solution was studied in this paper.The surface corrosion was recorded and the microstructures were examined by sc
Cyclic freeze-thaw has been recognized as one of the most primary factors leading to structure and function failure of concrete.Strain, which may have certain inherent advantages compared to tradition
During the hydration of cement tricalcium aluminate (C3A) reacts with gypsum and forms Ettringite (AFt).Once all gypsum is consumed ettringite can further react with remaining C3A and form monosulfate