【摘 要】
：
The production rate of REBa2Cu3O7-δ (REBCO) films could be improved effectively using metal-organic deposition by reducing fluorine content of the precurso
【机 构】
：
Shanghai Key Laboratory of High Temperature Superconductor,Shanghai,200444,China
论文部分内容阅读
The production rate of REBa2Cu3O7-δ (REBCO) films could be improved effectively using metal-organic deposition by reducing fluorine content of the precursor solution (CLF-MOD).To obtained high quality REBCO films using CLF-MOD,certain parameters of the thermal treatment process were optimized.In addition,a series of YxBa2Cu3O7-δ (x = 0.9,1.0,1.1,1.2,1.33,1.66) superconducting thin films were prepared on single crystal substrates and metal substrates (LaMnO3/MgO/Al2O3/Y2O3/Hastalloy) using LF-MOD in the present work.
其他文献
Spatial homogeneity in HTS tapes is one of the most important requirements for practical applications.However,the relationship between local critical curren
YBa2Cu3O7-δ(YBCO) coated conductor are highly expected as a promising candidate for high performance tapes which could be used at the liquid nitrogen tempe
Sumitomo Electric has been commercially producing the silver-sheathed Bi2223 multi-filamentary wires,especially under the name of DI-BSCCO (Dynamically-Inno
Long-length GdBCO coated conductors (CCs) possessing high critical current at 77 K in self field up to ~800 A/cm-width are being produced via a reactive co-
A stand-alone cryogenic test stand for testing new or newly-repaired superconducting radio-frequency (SRF) modules is extremely helpful to improve the SRF o
In the present work,the electro-deposition technique is realized as an effective,simple route to gain high-quality buffer layers for YBa2Cu3O7-δ(YBCO) coat
The superconducting,structural and mechanical properties of BSCCO bulk samples have been studied as a function of pressure by means of AC susceptibility,XRD
MgB2 wires have potential for future applications provided that sufficiently high current carrying capacity is made possible using low cost production metho
A high critical current density Jc is crucial for the application of HTS REBa2Cu3O7-δ (REBCO,RE = Y,Gd,Sm,etc.,rare earths) in the fabrication of energy ef
A high-quality buffer layer with flat surface and sharp bi-axial texture is of great important for YBCO coated conductor fabrication because YBCO nucleates