【摘 要】
：
In this study, volumetric deformation of gap-graded blended cement pastes with large amount of supplementary cementitous materials (SCMs) was investigated and compared with those of Portland cement an
【机 构】
：
School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640,
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
In this study, volumetric deformation of gap-graded blended cement pastes with large amount of supplementary cementitous materials (SCMs) was investigated and compared with those of Portland cement and reference blended cement pastes.The results show that the gap-graded blended cement pastes presented a higher initial packing density, therefore smaller amount of hydration products was needed to achieve dense microstructure,resulting in smaller chemical shrinkage.Notably, most of chemical shrinkage of gap-graded blended cements was occurred after the formation of skeleton structure, thus the autogenous shrinkage of gap-graded blended cements was reduced significantly due to restraint of the skeleton structure.Further, the microstructure of gap-graded blended cement pastes was dense and homogeneous due to grain size refinement and significant hydration of GBFS, and shrinkage stress was small and uniformly distributed.As a result, gap-graded blended cement pastes presented smaller volumetric deformation and superior resistance to cracking than Portland cement and interground blended cement pastes.
其他文献
The influence of a new type of antifreeze-reinforced material (AFRM) on Vc value, strength, freeze-thaw resistance, water absorptivity and void parameters of roller compacted concrete (RCC) were inves
Owing to environmental and commercial pressures the constitution of Portland cement formulations is changing towards having higher aluminosilicate contents.Mainly these changes are achieved by adding
Recycled concrete aggregates (RCA) are mainly composed of an intimate mix between natural aggregates and cement paste and the complete separation between these two phases is difficult.Cement paste gen
This study, a first contribution to research into low cost alternative cements explores the use ot various tractions of industrial by-products such as fly ash deposited in landfills.This new cement ha
The mortar specimens were prepared according to ISO 679: 2009.The cements used were ordinary Portland cement(OPC), high early strength Portland cement(HPC) and Portland blast furnace slag cement (clas
In this research the pozzolanic activity of commercial nanosilica was evaluated in lime pastes.Nanosilica samples used (suspension-NS and powder-Ny) were characterized by X-ray diffraction (XRD), part
A very important area in energy efficient construction is thermal insulation.Insulation has always been a demanding requirement when buildings are constructed, particularly in places where extreme cli
Supplementary cementitious materials (SCMs) are widely used in the concrete industry due to their economic and environmental advantages compared to systems containing solely Portland cement.Most of th
Slag is increasingly used for replacing a part of clinker.The addition of slag modifies the hydration process and so the physico-chemical properties (such as porosity, transport properties...) of ceme
The use of supplementary cementitious materials (SCMs) in blends with ordinary Portland cement (OPC) influences positively the workability, durability and strength of concrete, reduces the CO2 emissio