In order to solve the problem of the microscale charge withMEMS pyrotechnic devices,a new idea was proposed in this paper.Porous polymer fiber prepared with electrospin method was regarded as matrix w
The multicrystalline silicon wafers purified by directional solidification route were used to introduce copper impurities.The resistivity and minority carrier lifetime of multicrystalline silicon wafe
通对云无烟煤和烟煤分别进行1400℃,1700℃,2000℃,2200℃,2400℃和2600℃高温热处理,并对两种煤热处理产物的化学成分、电阻率、微观组织、物相成分和内部分子官能团迁移过程等进行了测试和表征,对比分析得出：煤中水分、灰分和挥发分等物相随热处理温度的提升逐渐转变并遗失,温度越高,物相转变越迅速,越彻底；热处理能使煤从一种近似绝缘相转变为导电相,温度越高导电相转化效果越好；煤的热处理
利用超声雾化热解沉积技术(USP)在不同温度的玻璃和电气石衬底上生长纳米ZnO薄膜.Raman和XRD结果表明晶体为六方纤锌矿多晶结构,衬底温度越高,Raman特征峰越强,晶体结晶性能越好,晶粒尺寸越大,C轴择优取向生长越明显.
A series of tourmaline/ZnO composite thin filmswere prepared by the facile route of low-temperature wet chemical method.X-ray diffraction (XRD)and Raman Spectroscopy analyses showed the hybrid spectro
采用水热法制备Ag@AgCl溶胶,并采用静电自组装技术在石英基片上通过交替提拉氧化石墨烯(GO)和Ag@AgCl溶胶,制备Ag@AgCl/GO复合薄膜并用做表面增强拉曼光谱基底。采用SEM,XRD,EDS,UV-vis以及共聚焦激光拉曼光谱测试仪对复合薄膜的结构及性能进行表征。
本文综述了近年来新型锂电池材料LiFePO4的不同制备方法，包括固相法、液相法和其他正在兴起的新方法，并且比较了各种方法的优缺点，指出了LiFePO4的研究方向和发展前景。
HfSiN/Cu/HfSiN/SiO2/Si multilayer films were prepared on Si substrate via magnetron sputtering technology.Annealing experiments of samples among 400℃ and 700℃ were carried out in order to investigate
本文采用一种可变电场调制的原子层沉积技术(E-ALD)制备了氧化锌(ZnO)薄膜。在前驱体脉冲时，通过施加不同大小和方向的电压，可以对制备所得ZnO薄膜的晶体择优取向和结晶性能进行可控调制。当在锌源脉冲时施加正电压，氧源脉冲时施加负电压，制备得到了c轴择优取向的薄膜。
本文首先分析了某电厂0Cr18Ni9不锈钢冷却水管发生穿孔的形貌和产生孔蚀的原因,并指出了在这种运行条件下防止孔蚀的措施。研究结果表明：0Cr18Ni9不锈钢冷却水管产生孔蚀的原因是水质中含有较多的Cl-和容易结垢的Ca2+、Mg2+,腐蚀的产物主要为Fe和Cr的氧化物；防止产生孔蚀的经济措施是提高水质的pH,并降低水质中的Ca2+、Mg2+含量。