【摘 要】
：
Calcium Silicate Hydrate compounds were synthesized by the reaction of lime and fumed silica.Different reaction conditions with varied temperature, Ca/Si ratio and reaction time were briefly conducted
【机 构】
：
School of Material Science and Engineering, University of Jinan, 250022, CHINA
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
Calcium Silicate Hydrate compounds were synthesized by the reaction of lime and fumed silica.Different reaction conditions with varied temperature, Ca/Si ratio and reaction time were briefly conducted with the product morphology characterized under SEM.In terms of temperature effect, the crystallinity at high temperature exhibited excellent but poor at low temperature.By changing the C/S ratio, the product obtained performed analogous under low temperature while diverse compounds were gained when the temperature was kept high.Moreover, the reaction time required differed too much as well.Under high temperature circumstance,short duration of reaction was sufficient for the good-quality crystal product produced.However, only poor-crystallined product could be formed even prolonged time of the reaction were conducted.Under SEM,good and poor crystallined product was distinguished and characterized.
其他文献
Alkali silica reaction, ASR is still a durability problem in Japan although countermeasures have been established since 1986.The problems of this Japanese situation are thought to be caused by lack of
The Ordinary Portland cement (OPC)-calcium aluminate cement (AC)-arhydrite (C (S)) system is useful for various construction materials because it can provide optimal physical properties by adjusting t
In recent years, alkali-activated slag (AAS) as an alternative low-carbon cementitious material has received increased attention.However, the high shrinkage and the crack tendency of AAS limit its wid
Reinforced concrete structures should be designed in order to resist all possible loading conditions and all predictable environmental impacts and combinations thereof during the entire design service
The structural condition of solidifying binding system has various thermodynamic stability and the degree ot ordering.It predetermines the tendency of these systems to self-organizing.Self-organizing
Low water requirement cements (LWRC) are a new type of hydraulic cements obtained by co-grinding of Portland cement clinker, gypsum and water reducing agent (plasticizer).During the grinding, in the p
A two-step manufacturing technology of composite nano-modified additive was developed.At the first stage a suspension was prepared by ultrasonic dispersion of MWCNT aggregates in isopropyl alcohol.At
The paper focuses on the effect of water cement ratio (w/c) on hydration of high porosity cement foams prepared by introducing preformed foam into Portland cement slurries, the relationship between st
The mechanical properties of cement paste containing waste paper fibers were investigated.The hydration degree and pore characteristic of cement paste were tested with TG-DSC (thermogravimetry-differe
For the time variation of C-S-H microstructure in steam curing concrete precast members and mass concrete, by using curing regime that simulates variable temperature process in interior of mass concre