In situ synchrotron X-ray radiography was used to study the effect of direct current(DC) on the grain nucleation and growth of Sn-50 wt.%Pb alloy. The results showed that applying DC adequately during solidification could effectively enhance the grain nucleation and inhibit its growth. Imaging of comparative experiments with varying DC intensity indicated that the final grain size, determined by the competition between grain nucleation and growth, was sensitively dependent on the DC intensity. It was found that the average grain size was decreased from 1632 to 567 μm with DC density of 1.5 A/mm~2 compared to the case without DC. Beyond this value, raising the current density may cause a significant decrease in the nucleation rate, and thus lead to a coarsening of the grain structure.
In situ synchrotron X-ray radiography was used to study the effect of direct current (DC) on the grain nucleation and growth of Sn-50 wt.% Pb alloy. The results showed that applying DC adequately during solidification could effectively enhance the grain nucleation and inhibit its growth. Imaging of comparative experiments with varying DC intensity indicated that the final grain size, determined by the competition between grain nucleation and growth, was sensitively dependent on the DC intensity. It was found that the average grain size was decreased from 1632 to 567 μm with DC density of 1.5 A / mm ~ 2 compared to the case without DC. Beyond this value, raising the current density may cause a significant decrease in the nucleation rate, and thus lead to a coarsening of the grain structure.