论文部分内容阅读
In this work, the mechanical properties and electrical conductivity of the extruded 7136 aluminum alloy treated by single-stage aging treatment (T6), retrogression and re-aging treatment (RRA), and multiple retrogression and re-aging treatment have been investigated by means of hard-ness measurements, electrical conductivity tests and tensile tests. The results have shown that the properties of the 7136 alloy such as hardness, tensile strength and electrical conductivity were sen-sitive to retrogression time (within 90 min). With prolonging the retrogression time, the tensile strength was enhanced first and then decreased, yet the electrical conductivity was continuously increased. The 60 min-treated alloy performed the highest tensile strength (716 MPa), whereas the 90 min-treated alloy possessed the highest electrical conductivity (33.95％IACS). Compared with the T6-treated alloy, the tensile strength and electrical conductivity were improved by 3.3％and 18.9％, respectively. The electrical conductivity showed an obvious increase with repetitious times of the RRA treatment. After 3RRA60 treatment, a good combination of tensile strength (705 MPa) and electrical conductivity (33.20％IACS) can be obtained. Compared with the T6 con-dition, the tensile strength and electrical conductivity were improved by 1.7％and 16.3％, respec-tively. The mechanism of microstructure evolution under different aging treatments has been discussed in detail.