The pearlitic transformation and the deformation behavior of lamellar cementite after cold rolling in eutectoid steels Fe-0.76%C-0.137%Mn(mass fraction) were studied by means of Formastor-F (Full Automatic Transformation Testing Instrument) and field emission scanning electronic microscopy (FESEM) observation. Fine and coarse pearlite were obtained in the eutectoid steels austenitized at 900℃ for 15min, then hold at 620℃ for 90 s and 690℃ for 7 h, respectively. The deformation behavior of cold rolled lamellar cementite could be classified as: cleavage fracture, inhomogeneous slip, fragmentation, thinning or necking, and homogeneous bending. The cementite lamellae with the thickness of more than 100 nm could be deformed plastically.
The pearlitic transformation and the deformation behavior of lamellar cementite after cold rolling in eutectoid steels Fe-0.76% C-0.137% Mn (mass fraction) were studied by means of Formastor-F (Full Automatic Transformation Testing Instrument) and field emission scanning electronic microscopy (FESEM) observation. Fine and coarse pearlite were obtained in the eutectoid steels austenitized at 900 ° C for 15 min, then hold at 620 ° C for 90 s and 690 ° C for 7 h, respectively. The deformation behavior of cold rolled lamellar cementite could be classified as: cleavage fracture, inhomogeneous slip, fragmentation, thinning or necking, and homogeneous bending. The cementite lamellae with the thickness of more than 100 nm could be deformed plastically.