论文部分内容阅读
Nano-structured layers are fabricated on the surface of 1.0C-1.5Cr steel by using the surface mechanical attrition treatment (SMAT) technology,and the microstructures of the surface nano-crystallization layers are characterized by means of X-ray diffraction (XRD) and transmission electron microscopy (TEM).The friction and wear properties are also investigated by a UMT-2 friction and wear tester.Experimental research has indicated that the average diameter of nanocrystalline grains in the surface layer after being treated for 15 min is in the range of 10-20 nm,and ferrite and cementite grains can not be identified by their morphologies.The wear-resistance of the specimen treated for 15 min has been doubled,compared with that of the matrix due to the grain refinement to a nano-sized scale.The lowest friction coefficient is 0.27,which is for the specimen treated for 30 min,resulting from the dissolution of the cementite phase and the formation of a relative homogenous structure.The SMAT technique for enhancing the wear-resistance of the 1.0C-1.5Cr steel has an optimum processing time,which is in the range of 15-30 min.The dominant wear mechanism of the specimen treated for 15 min changes from adhesive wear into particle wear.