【摘 要】
：
报道了TPU/LDPE/SBS共混材料的电性能和力学性能.探讨了共混比、乙炔炭黑用量对材料性能的影响 ;用透射电镜分析了该共混体系的结构.结果表明 ,该共混体系可以形成互穿网络结
论文部分内容阅读
报道了TPU/LDPE/SBS共混材料的电性能和力学性能.探讨了共混比、乙炔炭黑用量对材料性能的影响 ;用透射电镜分析了该共混体系的结构.结果表明 ,该共混体系可以形成互穿网络结构 ,从而强迫相容 ;在共混比为 10 /3/10 0时 ,乙炔炭黑用量为 2 2质量份可以制得综合性能优良的抗静电热塑性橡胶材料“,”A report was made on the electrical performances and the mechanical properties of TPU/LDPE/SBS antistatic blend. A discussion was also made on the influence of the blending ratio, the useful level of acetylene black on the properties of the blend, and the structure was analyzed with TEM. The results indicated that the blending system could form interpenetrating network and forced dissolve each other. As the blending ratio was 10/3/100 and the useful level of ACET was 22 Phr, a kind of thermoplastic antistatic TPU/LDPE/SBS blend was prepared, that had excellent comprehensive performance.
其他文献
在福建地区民间建筑中存在着许多利用可持续材料的实例,其中所展现的营建技巧和创作手法,体现了民间建设者改造环境、适应环境上的能力和智慧。本文就可持续材料的Reduce、Re
在氯丁橡胶中加入环化试剂AlEt2 Cl-C6H5CH2 Cl,在 12 0℃* 2 0min条件下 ,可制备环化氯丁橡胶.借助IR ,1H -NMR ,DSC ,GPC和裂解色谱测试方法对产物进行了表征.结果表明 ,二
:采用生物凝胶法处理无粉橡胶检查手套 ,成型后的胶膜先浸三价金属离子盐溶液 (4%硫酸铝溶液 ) ,再浸生物凝胶聚合物 ,最后用硅油进行外表面涂覆使手套无需经过水硫化、氯化等工序 ,制品表面滑爽“,”As treating free powder latex gloves with biology jellification, the shaping film first immersed salt solution of tri-valence metal ion(4%aluminum sulfate)
知名化学家、中国科学院化学部学部委员纪育沣先生逝世一周年之际,纪先生的夫人杨群华同志遵照纪先生生前的遗愿,将珍藏的全部科技文献刊物赠给中国科学院新疆化学研究所。
下沉式窑洞民居中蕴含了节能和可持续发展的生态理念,在消耗较低能源的情况下,室内具有较舒适的热微气候,能满足人体热舒适性的基本要求。本文通过实地测试结果和PMV模型对室
湖南属典型的山地、丘陵地形,气候温和湿润。文章从传统民居的结构、构造与材料工艺等方面研究了湖南民居的建造技术,指出湖南传统民居的建造技术是与其所处的地理环境、气候
研究了使用羧基丁腈胶乳制备工业手套 ,主要探讨了胶料配合 ,成膜等工艺流程.实验结果表明 :采用丁腈胶乳制备工业手套是完全可行的 ,所制得的制品胶膜均匀 ,柔软性好 ,色泽
介绍了泡沫型聚氨酯防压垫的配方和工艺过程“,”The formula and processing of the press resistant pillars of foam polyurethane were introduced.
雷谷川小流域村镇散居着欠发达的村镇人口,快速城市化进程中,经历着流域内部和流域之间迁徙的过程。本文以延安市雷谷川山地型聚落为例,以庭院为研究对象,探索了小流域聚落在
简述了基础隔震理论的发展情况 ,特别是对其中叠层橡胶隔震支座的国内外发展水平进行了对比分析 ,对该技术及产品的产业化进行展望