The influence of a gradient interlayer on the residual stress and cracking in TiN thin films was studied as a function of the thickness of gradient interlayer. Both X ray in situ tensile testing and grazing method were used to measure the residual stress in thin films. In TiN films, there exists a residual stress of 10 GPa, which can be remarkably decreased by a gradient interlayer between film and substrate. The cracking behavior of films after tension shows that the crack of film/substrate system begins at interface between film and substrate.
The influence of a gradient interlayer on the residual stress and cracking in TiN thin films was studied as a function of the thickness of gradient interlayer. Both X ray in situ tensile testing and grazing method were used to measure the residual stress in thin films. In TiN films, there exists a residual stress of 10 GPa, which can remarkably decreased by a gradient interlayer between film and substrate. The cracking behavior of films after tension shows that the crack of film / substrate system begins at interface between film and substrate.