【摘 要】
：
A little amount of aluminum substituting for Ni was added to Ti50Ni48Fe2 and Ti50Ni47.5Fe2.5 alloys to improve the mechanical properties, especially the yield s
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
A little amount of aluminum substituting for Ni was added to Ti50Ni48Fe2 and Ti50Ni47.5Fe2.5 alloys to improve the mechanical properties, especially the yield stress of the TiNiFe alloys. The martensitic transformation temperature and mechanical properties of Ti50Ni48-xFe2Alx and Ti50Ni47.5-xFe2.5Alx (x=0, 0.5, 1) alloys were examined, and it was revealed that 0.5% and 1%(mole fraction) aluminum addition lead to about 10℃ and 60-80 ℃ martensitic transformation temperature (MS) decrease, respectively. 1%(mole fraction) aluminum addition enhances remarkably the yield stresses of Ti50Ni47Fe2Al1 and Ti50Ni46.5Fe2.5Al1 to 560 and 580 MPa, respectively. The systemic microstructure analysis indicates that the second phase Ti2Ni at the grain boundaries plays an important role in improving the mechanical properties of TiNiFe shape memory alloys.
其他文献
Multi-walled carbon nanotubes were fabricated by the pyrolysis of acetylene with naturally occurring marine manganese nodules as a novel catalyst at an elevated
A rapid thermal process (RTP) was first introduced into the intrinsic gettering (IG) processes of fast neutron irradiated Czochralski (CZ) silicon. The effect o
The RE-aluminized coating and pure aluminized coating on 20 carbons steel were prepared by hot dip aluminizing method at 740 ℃. After diffusion treatment at 85
Video compression technologies are essential in video streaming application because they could save a great amount of network resources. However compressed vide
The paper describes an investigation into the volume change of cement mortar specimen at the three kinds of different curing schedules including 20℃ and 5% Na2
Mn-Zn spinel ferrites were synthesized by sol-gel method. Effects of calcined temperature on structure and particle size of MnZnFe2O4 were investigated by X-ray
The fretting behaviour of the AZ91D magnesium alloy was investigated. The influence of the number of cycles, normal load (contact pressure) and the amplitude of
Niobium-silicide alloys have great potential for high temperature turbine applications. The two-phase Nb/Nb5Si3 in situ composites exhibit a good balance in mec
A first-principles plane-wave pseudopotential method based on the density functional theory was used to investigate the energy and electronic structure of magne
Piezo crystals including quartz, quartz-like crystals, known and novel crystals of langasite-type structure were treated with density-functional perturb theory