论文部分内容阅读
Our recent studies concerning the binding of ionic surfactants on oppositely charged polyelectrolytes observedwith fluorescence techniques are reviewed. The cationic surfactants cetyltrimethylammonium bromide (CTAB),dodecyltrimethylammonium chloride (DTAC), and nonionic surfactant octaethylene glycol monododecyl ether (C_(12)E_8) wereallowed to bind on anionic poly(2-acrylamido-2-methylpropanesulfonic acid) (PAMPS) and its pyrene and/or naphthalenelabeled copolymers. The relative excimer emission intensity I_E/I_M of a cationic probe l-pyrenemethylamine hydrochloride(PyMeA·HCl) and the non-radiative energy transfer (NRET) I_(Py)/I_(Np) of naphthalene to pyrene for labeled polyelectrolyteswere chosen to monitor the binding process and the conformation change of surfactant-bound polyelectrolytes. The 1:1aggregation of polyelectrolyte-CTAB with respect to the charge was found as long as the CTAB concentration was slightlyhigher than its critical aggregation concentration (CAC). The intermolecular NRET indicated that the CTAB-boundpolyelectrolytes aggregated together through the hydrophobic interaction between the CTAB tails. However, neither 1:1polyelectrolyte-DTAC aggregation nor intermolecular aggregation of DTAC-bound polyelectrolyte was observed owing to itsweaker hydrophobicity of 12 carbon atoms in the tail, which is shorter than that of CTAB. As known from the fluorescenceresults, nonionic surfactant C_(12)E_8 did not bind on the anionic polyelectrolytes, but the presence of PAMPS promoted themicelle formation for C_(12)E_8 at the CAC slightly below its critical micelle concentration (CMC). The solid complex of dansyllabeled AMPS copolymer-surfactant exhibited a decrease in local polarity with increasing charge density of thepolyelectrolyte or with alkane tail length of the surfactant. SAXS suggested a lamella structure for the AMPS copolymer-surfactant solid complexes with a long period of 3.87 nm for CTAB and 3.04 nm for DTAC, respectively.
We have been researching the binding of ionic surfactants on oppositely charged polyelectrolytes observedwith fluorescence techniques were reviewed. The cationic surfactants cetyltrimethylammonium bromide (CTAB), dodecyltrimethylammonium chloride (DTAC), and nonionic surfactant octaethylene glycol monododecyl ether (C_ (12) E_8) wereallowed to (PAMPS) and its pyrene and / or naphthalenelabeled copolymers. The relative excimer emission intensity I_E / I_M of a cationic probe l-pyrenemethylamine hydrochloride (PyMeA.HCl) and the non -radiative energy transfer (NRET) I_ (Py) / I_ (Np) of naphthalene to pyrene for labeled polyelectrolytes were chosen to monitor the binding process and the conformation change of surfactant-bound polyelectrolytes. The 1: 1 aggregation of polyelectrolyte-CTAB with respect to the charge was found as long as the CTAB concentration was slightlyhigher than its critical aggregation concentration (CAC). The inter molecular NRET indicated that the CTAB-bound polyelectrolyte was aggregated through the hydrophobic interaction between the CTAB tails. However, neither 1: 1 polyelectrolyte-DTAC aggregation nor intermolecular aggregation of DTAC-bound polyelectrolyte was observed to to be weaker hydrophobicity of 12 carbon atoms in the tail, which is shorter than that of CTAB. As known from the fluorescence results, nonionic surfactant C_ (12) E_8 did not bind on the anionic polyelectrolytes, but the presence of PAMPS promoted themicelle formation for C_ (12) E_8 at the CAC slightly below its critical micelle concentration (CMC). The solid complex of dansyllabeled AMPS copolymer-surfactant exhibited a decrease in local polarity with increasing charge density of the polyer or with alkane tail length of the surfactant. SAXS suggested a lamella structure for the AMPS copolymer-surfactant solid complexes with a long period of 3.87 nm for CTAB and 3.04 nm for DTAC, respectively.