摘 要：随着近年来水利工程施工工艺的改革和发展，堰体滑模、大模板、框架结构等体系的普遍应用，水利工程中混凝土施工的比重也越来越大，同时混凝土工程的质量也越来越受到重视，因此怎样保证混凝土工程的施工质量，防治现浇混凝土的质量通病，成为提高工程质量的重中之重。本文结合工作实际，对水工混凝土质量通病产生原因及防治措施进行探讨。
关键词水工混凝土；质量通病；防治措施
Abstract: in recent years, with water conservancy project construction process of reform and development, sliding mode, big template, pointed frame structure of the system and widely used in water conservancy engineering the proportion of concrete construction is more and more big, at the same time, the quality of concrete engineering, more and more attention, so how to ensure the construction quality of concrete engineering, prevention and control of cast-in-situ concrete quality problems become improving engineering quality is the most important thing. Based on the working practice, hydraulic concrete quality problems of causes and prevention and control measures are discussed.
Key words hydraulic concrete; The common faults; Prevention and control measures
中图分类号：[TU528.36] 文献标识码：A文章编号：
一、 前言
水工混凝土的耐久性直接关系到工程的使用寿命、加固费用、效益发挥和运行安全，但是水工混凝土却经常受到裂缝、冻胀、冲磨和空蚀、碱骨科反应、碳化、溶蚀和侵蚀等病害的威胁，由于工程耐久性不足，增加了建筑物使用过程中的修理与加固费用，影响或限制了结构的正常使用功能并缩短结构的使用年限，影响效益和安全，不仅造成经济损失，而且严重浪费资源，引发社会问题。因此有必要对水工混凝土的常见病害进行分析和研究，并反馈到设计、施工和运行管理等方面未进行预防和控制，在工程建设管理的整个过程中，全方位、多渠道地提高水工混凝土的质量和耐久性，延长工程使用寿命。
二、水工混凝土常见质量缺陷产生原因及其防治措施
1 蜂窝
1．1 产生原因
(1)混凝土配合比不当或砂、石子、水泥、加水量计量不准，造成砂浆少、石子多；
(2)混凝土搅拌时间不够，未拌合均匀，和易性差，振捣不密实；
(3)下料不当或下料过高，未设串筒，致使石子集中，造成石子砂浆离析；
(4)混凝土未分层下料，振捣不实，或漏振，或振捣时间不够；
(5)模板缝隙未堵严，水泥浆流失；
(6)钢筋较密，使用的石子粒径过大或坍落度过小；
(7)基础、柱、墙根部未稍留间歇就继续浇灌上层混凝土。
1．2 防治措施
(1)认真设计、严格控制混凝土配合比，经常检查，做到计量准确，混凝土拌合均匀，坍落度适中；混凝土下料高度超过2m应设串筒或溜槽，浇灌应分层下料，分层振捣，防止漏振；模板缝应堵塞严密，浇灌中，应随时检查模板支撑情况防止漏浆；基础、柱、墙根部应在下部浇完间歇1～1．5h，沉实后再浇上部混凝土。
(2)蜂窝处理：对于非过水面的一般蜂窝，先进行凿毛，洗刷干净后，用1：2或1：2．5水泥砂浆压实抹平；对于过水面的一般蜂窝，先进行凿毛，洗刷干净后，用环氧砂浆压实抹平，再用环氧基液涂面。较大蜂窝，凿去蜂窝处薄弱松散颗粒，刷洗干净后，支模用高一强度等级的细石混凝土仔细填塞捣实，待混凝土凝固后用砂轮进行适度打磨，保证表面平顺和色泽相近。较深蜂窝，如清除困难，可埋灌浆管、排气管，表面支模浇筑高一强度等级的细石混凝土封闭凝固后，进行水泥灌浆处理。
2 麻面
2．1 产生原因
(1)模板表面粗糙或粘附水泥浆渣等杂物未清理干净，拆模时混凝土表面被粘坏；
(2)模板未浇水湿润或湿润不够，构件表面混凝土的水分被吸去，使混凝土失水过多出现麻面；
(3)摸板拼缝不严，局部漏浆；
(4)模扳隔离剂涂刷不匀，或局部漏刷或失效，混凝土表面与模板粘结造成麻面；
(5)混凝土振捣不实，气泡未排出，停在模板表面形成麻点。
2．2 防治措施
(1)模板表面清理干净，不得粘有干硬水泥砂浆等杂物。浇灌混凝土前，模板应浇水充分湿润，模板缝隙，应用油毡纸、腻子等堵严，模扳隔离剂应选用长效的，涂刷均匀，不得漏刷；混凝土应分层均匀振捣密实，至排除气泡为止。
(2)麻面处理：对于非过水的麻面，用钢丝刷加清水刷洗，使麻面部位充分湿润，用原混凝土配合比去石子砂浆压实抹平，待其凝固后用手持砂轮进行适度打磨，保证表面平顺和色泽相近。对于过水的麻面，处理措施与非过水的基本相同，最后，待砂浆达到龄期强度后再涂刷环氧基液两遍，以保证修补部位有足够的耐磨度，防止高速水流产生气蚀。
3 露筋
3.1产生原因
(1)浇筑混凝土时，混凝土保护层垫块位移或垫块太少或漏放，致使钢筋紧贴模板外露；
(2)结构构件截面小，钢筋过密，石子卡在钢筋上，使水泥砂浆不能充满钢筋周围，造成露筋；
(3)混凝土配合比不当，产生离折，靠模板部位缺浆或模板漏浆；
3．2 防治措施
(1)浇筑混凝土前，应保证钢筋位置和保护层厚度正确，并加强检查验证。钢筋密集处，应选用适当粒径的石子，保证混凝土配合比准确及良好的和易性；浇筑高度超过2m时，应用串筒或溜槽进行下料，防止离析；模板应充分湿润并认真堵好缝隙；混凝土振捣严禁撞击钢筋，操作时，避免踩踏钢筋，如有踩弯或脱扣等及时调整扶正；保护层混凝土要振捣密实；正确掌握脱模时间，防止过早拆模，碰坏棱角。
(2)露筋处理：对于非过水面的表面漏筋，刷洗干净后，在表面抹1：2或1：2．5水泥砂浆，将漏筋部位抹平，待砂浆凝固后用砂轮进行适度打磨，保证表面平顺和色泽相近。对于过水面的表面漏筋，处理措施与非过水的基本相同，最后，待砂浆达到龄期强度后再涂刷环氧基液两遍，以保证修补部位有足够的耐磨度。
4 缺棱掉角
4．1 产生原因
(1)木模板未充分浇水湿润或湿润不够，混凝土浇筑后养护不好，造成脱水，强度低，或模板吸水膨胀将边角拉裂，拆模时，棱角被粘掉；
(2)低温施工过早拆除侧面非承重模板；
(3)拆模时，边角受外力或重物撞击，或保护不好，棱角被碰掉；
4．2 防治措施
(1)木模板在浇筑混凝土前应充分湿润，混凝土浇筑后应认真洒水养护。拆除侧面非承重模板时，混凝土应具有1．2MPa以上的强度；拆模时注意保护棱角，避免用力过猛过急；吊运模板，防止撞击棱角，运输时，将成品阳角用草袋等保护好，以免碰损。
(2)缺棱掉角，可将缺陷处松散颗粒凿除，冲洗干净并充分湿润后，视破損程度用1：2或1：2．5水泥砂浆抹补齐平，或支模浇筑高一强度等级的混凝土，捣实密实，待混凝土凝固后用砂轮进行适度打磨，保证表面平顺和色泽相近。
三、结语
由于病害的影响，很多水工混凝土建筑物的耐久性受到威胁和挑战，很多以前建成的混凝土建筑物也不同程度地遭受了破坏，因此很有必要对这些病害进行分析和研究论证，探讨可行的有效的处理措施和预控方案，并且在工程建设过程中做好宣传教育和引导。混凝土的耐久性问题不是设计、施工和运行管理单位任何一家的问题，而是大家面临的共同问题，我们一定要高度重视，认真对待，各参建及运行管理单位要齐心协力，全方位、多渠道地联合控制，确保混凝土质量，减少病害隐患及威胁，提高水工混凝土耐久。
关键词水工混凝土；质量通病；防治措施
Abstract: in recent years, with water conservancy project construction process of reform and development, sliding mode, big template, pointed frame structure of the system and widely used in water conservancy engineering the proportion of concrete construction is more and more big, at the same time, the quality of concrete engineering, more and more attention, so how to ensure the construction quality of concrete engineering, prevention and control of cast-in-situ concrete quality problems become improving engineering quality is the most important thing. Based on the working practice, hydraulic concrete quality problems of causes and prevention and control measures are discussed.
Key words hydraulic concrete; The common faults; Prevention and control measures
中图分类号：[TU528.36] 文献标识码：A文章编号：
一、 前言
水工混凝土的耐久性直接关系到工程的使用寿命、加固费用、效益发挥和运行安全，但是水工混凝土却经常受到裂缝、冻胀、冲磨和空蚀、碱骨科反应、碳化、溶蚀和侵蚀等病害的威胁，由于工程耐久性不足，增加了建筑物使用过程中的修理与加固费用，影响或限制了结构的正常使用功能并缩短结构的使用年限，影响效益和安全，不仅造成经济损失，而且严重浪费资源，引发社会问题。因此有必要对水工混凝土的常见病害进行分析和研究，并反馈到设计、施工和运行管理等方面未进行预防和控制，在工程建设管理的整个过程中，全方位、多渠道地提高水工混凝土的质量和耐久性，延长工程使用寿命。
二、水工混凝土常见质量缺陷产生原因及其防治措施
1 蜂窝
1．1 产生原因
(1)混凝土配合比不当或砂、石子、水泥、加水量计量不准，造成砂浆少、石子多；
(2)混凝土搅拌时间不够，未拌合均匀，和易性差，振捣不密实；
(3)下料不当或下料过高，未设串筒，致使石子集中，造成石子砂浆离析；
(4)混凝土未分层下料，振捣不实，或漏振，或振捣时间不够；
(5)模板缝隙未堵严，水泥浆流失；
(6)钢筋较密，使用的石子粒径过大或坍落度过小；
(7)基础、柱、墙根部未稍留间歇就继续浇灌上层混凝土。
1．2 防治措施
(1)认真设计、严格控制混凝土配合比，经常检查，做到计量准确，混凝土拌合均匀，坍落度适中；混凝土下料高度超过2m应设串筒或溜槽，浇灌应分层下料，分层振捣，防止漏振；模板缝应堵塞严密，浇灌中，应随时检查模板支撑情况防止漏浆；基础、柱、墙根部应在下部浇完间歇1～1．5h，沉实后再浇上部混凝土。
(2)蜂窝处理：对于非过水面的一般蜂窝，先进行凿毛，洗刷干净后，用1：2或1：2．5水泥砂浆压实抹平；对于过水面的一般蜂窝，先进行凿毛，洗刷干净后，用环氧砂浆压实抹平，再用环氧基液涂面。较大蜂窝，凿去蜂窝处薄弱松散颗粒，刷洗干净后，支模用高一强度等级的细石混凝土仔细填塞捣实，待混凝土凝固后用砂轮进行适度打磨，保证表面平顺和色泽相近。较深蜂窝，如清除困难，可埋灌浆管、排气管，表面支模浇筑高一强度等级的细石混凝土封闭凝固后，进行水泥灌浆处理。
2 麻面
2．1 产生原因
(1)模板表面粗糙或粘附水泥浆渣等杂物未清理干净，拆模时混凝土表面被粘坏；
(2)模板未浇水湿润或湿润不够，构件表面混凝土的水分被吸去，使混凝土失水过多出现麻面；
(3)摸板拼缝不严，局部漏浆；
(4)模扳隔离剂涂刷不匀，或局部漏刷或失效，混凝土表面与模板粘结造成麻面；
(5)混凝土振捣不实，气泡未排出，停在模板表面形成麻点。
2．2 防治措施
(1)模板表面清理干净，不得粘有干硬水泥砂浆等杂物。浇灌混凝土前，模板应浇水充分湿润，模板缝隙，应用油毡纸、腻子等堵严，模扳隔离剂应选用长效的，涂刷均匀，不得漏刷；混凝土应分层均匀振捣密实，至排除气泡为止。
(2)麻面处理：对于非过水的麻面，用钢丝刷加清水刷洗，使麻面部位充分湿润，用原混凝土配合比去石子砂浆压实抹平，待其凝固后用手持砂轮进行适度打磨，保证表面平顺和色泽相近。对于过水的麻面，处理措施与非过水的基本相同，最后，待砂浆达到龄期强度后再涂刷环氧基液两遍，以保证修补部位有足够的耐磨度，防止高速水流产生气蚀。
3 露筋
3.1产生原因
(1)浇筑混凝土时，混凝土保护层垫块位移或垫块太少或漏放，致使钢筋紧贴模板外露；
(2)结构构件截面小，钢筋过密，石子卡在钢筋上，使水泥砂浆不能充满钢筋周围，造成露筋；
(3)混凝土配合比不当，产生离折，靠模板部位缺浆或模板漏浆；
3．2 防治措施
(1)浇筑混凝土前，应保证钢筋位置和保护层厚度正确，并加强检查验证。钢筋密集处，应选用适当粒径的石子，保证混凝土配合比准确及良好的和易性；浇筑高度超过2m时，应用串筒或溜槽进行下料，防止离析；模板应充分湿润并认真堵好缝隙；混凝土振捣严禁撞击钢筋，操作时，避免踩踏钢筋，如有踩弯或脱扣等及时调整扶正；保护层混凝土要振捣密实；正确掌握脱模时间，防止过早拆模，碰坏棱角。
(2)露筋处理：对于非过水面的表面漏筋，刷洗干净后，在表面抹1：2或1：2．5水泥砂浆，将漏筋部位抹平，待砂浆凝固后用砂轮进行适度打磨，保证表面平顺和色泽相近。对于过水面的表面漏筋，处理措施与非过水的基本相同，最后，待砂浆达到龄期强度后再涂刷环氧基液两遍，以保证修补部位有足够的耐磨度。
4 缺棱掉角
4．1 产生原因
(1)木模板未充分浇水湿润或湿润不够，混凝土浇筑后养护不好，造成脱水，强度低，或模板吸水膨胀将边角拉裂，拆模时，棱角被粘掉；
(2)低温施工过早拆除侧面非承重模板；
(3)拆模时，边角受外力或重物撞击，或保护不好，棱角被碰掉；
4．2 防治措施
(1)木模板在浇筑混凝土前应充分湿润，混凝土浇筑后应认真洒水养护。拆除侧面非承重模板时，混凝土应具有1．2MPa以上的强度；拆模时注意保护棱角，避免用力过猛过急；吊运模板，防止撞击棱角，运输时，将成品阳角用草袋等保护好，以免碰损。
(2)缺棱掉角，可将缺陷处松散颗粒凿除，冲洗干净并充分湿润后，视破損程度用1：2或1：2．5水泥砂浆抹补齐平，或支模浇筑高一强度等级的混凝土，捣实密实，待混凝土凝固后用砂轮进行适度打磨，保证表面平顺和色泽相近。
三、结语
由于病害的影响，很多水工混凝土建筑物的耐久性受到威胁和挑战，很多以前建成的混凝土建筑物也不同程度地遭受了破坏，因此很有必要对这些病害进行分析和研究论证，探讨可行的有效的处理措施和预控方案，并且在工程建设过程中做好宣传教育和引导。混凝土的耐久性问题不是设计、施工和运行管理单位任何一家的问题，而是大家面临的共同问题，我们一定要高度重视，认真对待，各参建及运行管理单位要齐心协力，全方位、多渠道地联合控制，确保混凝土质量，减少病害隐患及威胁，提高水工混凝土耐久。