Room temperature deformation behavior of A1-8Fe-2Mo-2V-1Zr alloy produced by spray forming and subsequent warm-extrusion at 693 K and/or rolling at 423 K was in
【机 构】
：
Advanced Materials R&D Center,School of Materials Science and Engineering
论文部分内容阅读
Room temperature deformation behavior of A1-8Fe-2Mo-2V-1Zr alloy produced by spray forming and subsequent warm-extrusion at 693 K and/or rolling at 423 K was investigated in terms of tensile test and microstructural observation.In the specimen processed by spray forming and warm extrusion, the microstructure consisting of equiaxed grains with the average grain size of 500 nm in the matrix phase and uniformly dispersed fine intermetallic A13(Fe, Mo, V, Zr) and A16(Fe, Mo, V, Zr) phases less than 100 nm was characterized. It was revealed that subsequent warm rolling after warm extrusion promotes precipitation of a fine dispersoid from the supersaturated matrix phase. Warm rolling was found to be effective to increase the yield and tensile strength in the high strain rate regime. Elongation of the warm rolled specimen showed highe r value than extruded specimen over the whole strain rate region studied.
其他文献
以低熔点Pb-Sn-Bi合金作为钢液模拟工质,对谐波高频磁场作用下,方坯软接触电磁连铸结晶器内钢液的弯月面行为进行热模拟实验研究.通过录像手段记录高频磁场作用下非导电石英
The key technology and the main mechanism of microcrystallizing leucite to reirforce dentalglass ceramics were investigated. The feedstock powders were selected
The experimental researches on the chemical deposition of Ni-Mo-P amorphous alloys were carried out by adding Na2 MoO4 into acidic solutions. The optimum techno
The changes in mechanical properties and fracture toughness by dynamic loading were investigated with experiments.The parameter R, which can reflect the effect
The oxidation behavior of Ni-Cr-Al-Y coating produced by multi-arc ion plating with and without an enamel coating was investigated in flow oxygen and oxygen con
Cerium addition plays an important role in sintering, transformation and phasicochemical properties of cordierite ceramics. The present work aims at studying th
The fabrication process of Sm2O3 doped CeO2 reinforced Ti3AlC2 nano composites including the nano particle dispersion process by a hetero-coagulation process wa
Fine ground powders of Nd-Fe-B sintered magnet bulks(particle size=46～125 μm in diameter) were coated and alloyed with Yb metal by sorbing them. A significant r
This paper proposes a new untraceable Partially Blind Signature scheme which is a cross between the traditional signature scheme and the blind signature scheme.
Ferrography is deemed as one of the most effective methods for wear particle analysis and failure diagnosis. By analyzing the configuration, content and composi