有机蒙脱土增强聚氯乙烯手套材料的制备与表征

• 作 者: 孙春鹏 宋国君 王立 罗鹏 葛棚 赵伟 马培育 陈林
• 机 构: 青岛大学高分子材料研究所,青岛华夏橡胶工业有限公司,
• 出 处: 精细与专用化学品
• 发表日期: 2012年05期
• 关键词: 纳米复合材料 有机蒙脱土 乳液PVC

通过在乳液聚氯乙烯(PVC)中添加有机蒙脱土(OMMT)来研究OMMT对其各项性能的影响。结果表明:OMMT对乳液PVC/邻苯二甲酸二辛酯(DOP)/OMMT纳米复合材料的力学性能有一定的改善效果;对复合材料的抗增塑剂迁移效果明显;在耐酸和耐碱试验中,未添加OMMT的复合材料的拉伸强度和撕裂强度分别降低了7.3%、5.1%和5.5%、13.3%,而添加3份OMMT后,仅仅降低了2.5%、2.6%和1.5%、4.2%,效果显著。

The effect of OMMT on its properties was investigated by adding OMMT to emulsion polyvinyl chloride (PVC). The results show that OMMT can improve the mechanical properties of PVC / DOP / OMMT nanocomposites. The effect of OMMT on the plasticizer migration is obvious. In the acid and alkali resistance test , The tensile strength and tear strength of OMMT-free composites decreased by 7.3%, 5.1% and 5.5%, 13.3%, respectively, but decreased by 2.5%, 2.6% and 1.5% after 3 OMMT additions, 4.2%, the effect is remarkable.