SiO2包覆超细CaCO3的微晶分析和XPS研究

• 作 者: 华益苗 袁骏 岳林海 蔡菊香
• 机 构: 浙江大学玉泉校区化学系! 杭州 310027,浙江大学玉泉校区化学系! 杭州 310027,浙江大学玉泉校区化学系! 杭州 310027,浙江大学玉泉校区化学系! 杭州 310027
• 出 处: 无机化学学报
• 发表日期: 2001年01期
• 关键词: XPS XRD 超细 CaCO3 包覆 SiO2

： The superfine CaCO3 powder coated with SiO2 was synthesized. Through XRD technique, the cell parameters and crystallite size of reference and coated CaCO3 were calculated. SiO2 present in the state of amorphous and prevent the agglomeration and growth of CaCO3 micro-crystal. By comparing the result of XPS analysis of reference compound to coated sample, CaCO3 has been coated successfully with SiO2. The thickness of the coating is about 2.4～ 3.4nm. From the difference(0.8eV increase) of the binding energy of Ca2p, we presume that the bind Si-O-Ca has formed in the surface of CaCO3.

The superfine CaCO3 powder coated with SiO2 was synthesized. Through XRD technique, the cell parameters and crystallite size of reference and coated CaCO3 were calculated. SiO2 present in the state of amorphous and prevent the agglomeration and growth of CaCO3 micro-crystal. the result of XPS analysis of reference compound to coated sample, CaCO3 has been coated successfully with SiO2. The thickness of the coating is about 2.4-3.4 nm. From the difference (0.8eV increase) of the binding energy of Ca2p, we presume that the bind Si-O-Ca has formed in the surface of CaCO3.