Growth of Superconducting YBCO Crystals with High Tc

• 作 者: 王弘 徐斌 尚淑霞 杨兆荷 宋永远 于文涛 杨忠森 王卓 李翠萍 梅梁模
• 机 构: Shangdon University,Jinan,Shangdon University,Jinan,Shangdon University,Jinan,Shangdon University,Ji
• 出 处: 人工晶体
• 发表日期: 1988年Z1期
• 关键词: YBCO diffractometer tempera stoichiometric have squared likely firmly molar unde

Single crystals of YBCO were grown from non-stoichiometric mixture ofY-Ba-Cu-O system.Crystals obtained have plate like shape with squared cor-ners,and the largest size is 2.5×2.0×0.1mm~3.The crystal structure ofYBCO was determined by Nic XRD-P3/R3 diffractometer at room tempera-

Single crystals of YBCO were grown from non-stoichiometric mixture of Y-Ba-Cu-O system. Crystals were obtained with plate like shape with squared cor-ners, and the largest size was 2.5 × 2.0 × 0.1mm ~ 3. The crystal structure of YBCO was determined by Nic XRD-P3 / R3 diffractometer at room tempera-