【摘 要】
：
研究开发了FeCrMoAlWCu不锈钢,与传统的Fe-Cr-Al-Mo耐热钢相比,Mo含量较高,Al含量较低。研究表明,其具有体心立方(BCC)结构,合金耐腐蚀性能良好,室温下在3.5%的NaCl溶液中的
论文部分内容阅读
研究开发了FeCrMoAlWCu不锈钢,与传统的Fe-Cr-Al-Mo耐热钢相比,Mo含量较高,Al含量较低。研究表明,其具有体心立方(BCC)结构,合金耐腐蚀性能良好,室温下在3.5%的NaCl溶液中的点蚀电位约为0.915 V,与00Cr26Ni6Mo4CuTi不锈钢相当。在1 100℃下的空气环境中具有良好的抗氧化性,经过100h的高温氧化试验,其单位面积质量增加约为0.428 4g/m~2,优于Cr_(23)Al_5合金。
The FeCrMoAlWCu stainless steel has been researched and developed. Compared with the traditional Fe-Cr-Al-Mo heat-resistant steel, Mo content is higher and Al content is lower. The results show that the alloy has the structure of BCC and the corrosion resistance of the alloy is good. The pitting potential in 3.5% NaCl solution at room temperature is about 0.915 V, which is comparable to that of 00Cr26Ni6Mo4CuTi stainless steel. In 100 ℃ air environment has good oxidation resistance, after 100h high temperature oxidation test, the mass per unit area increased about 0.428 4g / m ~ 2, better than the Cr 23 Al 5 alloy.
其他文献
以金属型铸造铝合金导电杆为例,对铸件的凝固过程进行数值模拟,可以直观地发现因结构不合理导致的铸造缺陷以及定量化分析铸造缺陷,为优化铸件结构提供参考。采用优化的金属
采用液态搅拌铸造制出了纤维长度分别为2mm和3mm、含量为2%的短碳纤维增强的含Sc的2024铝基复合材料。用加载-卸载法研究了两种材料不同时效态的微屈服性能。结果表明,短碳纤
采用铸锻复合一体化成形技术制备了AZ91D镁合金,研究了锻压变形量对AZ91D镁合金组织与力学性能的影响。结果表明,锻压变形量越大,锻压对模具型腔内凝固过程的AZ91D镁合金的强
目的探讨运动平板试验在诊断冠心病中的意义。方法随机选取我院2009年～2010年住院患者中疑似冠心病的100例患者,在2周内先后对其进行运动平板试验检查和冠状动脉照影。结果运
在Mg93Zn6Y1合金凝固过程中施加脉冲磁场处理,主要研究了放电电压对Mg93Zn6Y1合金组织和力学性能的影响。结果表明,施加脉冲磁场对Mg93Zn6Y1合金凝固组织中的初生α-Mg相和准
研究了不同含量Yb部分替换Zr对热挤十冷轧态Al-0.2Sc-0.04(Zr,Yb)合金力学性能和导电性的影响.发现只有Yb含量为0.01％和0.02％的Al-0.2Sc-0.04(Zr,Yb)合金具有明显的时效强化峰,
主要研究了0.1％的Al92 Mn6 Ce2铸态中间合金和Al92 Mn6 Ce2非晶条带中间合金对A356铝合金的细化变质效果,以及经过T6处理之后对其组织的影响.结果表明,加入0.1％的铸态中间合金A
目的 探讨血清同型半胱氨酸水平(HCY)及尿微量白蛋白(UMA)联合检测对糖尿病患者(DM)早期肾损伤诊断价值.方法 研究122例DM及34例糖尿病肾病患者(DN)和42例健康对照组的HCY及U
采用热压烧结+热挤压法制备了不同SiC_p含量的Al基复合材料,运用XRD、SEM、TEM等研究了不同SiC_p含量的Al基复合材料的显微组织和力学性能,并对断口形貌进行了观察。结果表明
研究了不同真空度下AlSiMgMn压铸件在铸态、T1、T5和T6热处理后的力学性能。结果表明,铸态下,高真空(真空度为95~97kPa时)铸件的伸长率是普通压铸件的2.3倍;T1处理后,高真空