【摘 要】
：
The room temperature creep behaviors of Mg61Cu28Gd11 and (Mg61Cu28Gd11i)99.5Sb0.5 bulk metallic glasses (BMGs) were revealed by means of nanoindentation techniq
【机 构】
：
College of Materials Science and Technology
论文部分内容阅读
The room temperature creep behaviors of Mg61Cu28Gd11 and (Mg61Cu28Gd11i)99.5Sb0.5 bulk metallic glasses (BMGs) were revealed by means of nanoindentation technique. The creep mechanism was explored by characterization of creep rate sensitivity, creep compliance and retardation spectra. The results showed that the experimental creep curves could be well described by a generalized Kelvin model. The low creep rate sensitivity of both Mg-based BMGs indicated that their room temperature creep was dominated by localized shear flow. In addition, the (Mg61Cu28Gd11)99.5Sb0.5 glassy alloy exhibited lower creep rate sensitivity, creep compliance and milder retardation peak, indicating its higher creep-resistance and less relaxed state. Furthermore, the creep retardation spectrum consisted of two relatively separated peaks with the well defined characteristic relaxation times.
其他文献
采用水热法在180℃下反应36 h合成了具有规整八面体状的烧绿石结构La2Sn2O7:Eu3+微晶.采用XRD、TEM、SEM、EDS、FT-IR、Raman和PL对合成产物的晶体结构、颗粒尺寸、形貌和光
In the purification process of automobile exhaust, existing water plays an important role as an oxidant, which converts CO and hydrocarbons (HCs) by the water-g
在温度为300-450℃和应变速率为0.01-10 s-1的变形条件下,对Al-Zn-Mg-Cu-Zr合金(7056和7150铝合金)进行热压缩实验.结果表明:在一定的应变峰值出现后,流动应力随应变增加单调
硼酸铝晶须增强6061铝合金基复合材料中的界面反应影响其断口分形维数.该复合材料由压力铸造法制备,采用垂直剖面法分析拉伸断裂断口.当量尺度分别取3-15μm以及1-5μm时,可
A new type of Cu-La2O3 composite was fabricated by internal oxidation method using powder metallurgy. Sliding wear behavior of the Cu-La2O3 composite was studie
The neodymium trifluoroacetate complexes were synthesized and characterized by single-crystal X-ray diffraction for [Nd(CF3COO)3·Bpy·(H2O)3]Bpy (1), elemental
Polycrystalline Ndo. 75Na0.25Mn1-xCrxO3 (0≤x≤.1) samples were prepared by sol-gel method and their magnetic and electrical transport properties were investiga
采用放电等离子烧结(SPS)技术固结成形W-5.6Ni-1.4Fe(质量分数,%)混合粉末,研究不同加热速率对烧结致密化行为和微观组织演变规律的影响.结果表明,W-5.6Ni-1.4Fe合金的SPS致
The blade frequency noise of non-cavitation propeller in a uniform flow is analyzed in time domain.The unsteady loading (dipole source) on the blade surface is
采用响应曲面法中的中心组合模式对偏钒酸铵煅烧制备V2O5工艺条件进行优化,建立偏钒酸铵煅烧制备V2O5的二次多项式数学模型,探讨主要因素的影响及其交互作用.方差分析结果表