【摘 要】
：
The single-crystalline nickel nanorods with narrow size distribution and better magnetic properties were synthesized by thermal decomposition of nickel hydroxid
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
The single-crystalline nickel nanorods with narrow size distribution and better magnetic properties were synthesized by thermal decomposition of nickel hydroxide nanorods precursor powders,which were produced by soft template method using nickel oxalic acid as raw material. The influences of hydrothermal reaction temperature and time on morphology of the products were investigated. The structure,morphology and magnetic properties of the products were characterized by X-ray powder diffraction (XRD),transmission electron microscopy (TEM),thermogravimetric differential scanning calorimetry (TGA-DSC) and vibrating sample magnetometer (VSM). The as-prepared nickel nanorods are uniform with a diameter of 10-15 nm and length 70-120 nm. The results of magnetic measurements show that the specific saturation magnetization(ós) and coercivity values(Hc) of the nickel nanorods are 50.649 A·m2/kg and 190.0×(103/4π)A/m,respectively. Finally,a possible mechanism for the formation of nickel nanorods was discussed briefly.
其他文献
In order to improve the prediction capability of spring-back in aluminum sheet metal forming, the influence of the plastic deformation on elastic modulus is con
The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation (MAO) was characterized. The results show that the ceramic coating(3.4-23 μm in thick
By electrical resistance tomography (ERT) the cross sectional profiles of gas hold-up in a φ56mm bubble colunmn are obtained with four designs of gas sparger.
Fouling-resistant ceramic-supported polymer composite membranes were developed for removal of oil-in-water (O/W) microemulsions. The composite membranes were fe
Free radical co-polymerization was employed to synthesize co-poly carboxylate (PC) superplasticizers with different amount of carboxyl and methyl polyethylene g
Alumina sols with a mlar ratio of 1: 50 between aluminum sec- butoxide ( ASB ) and H2 O werefabricated by adding various amounts of nitric acid.The particle sha
A laboratory study was undertaken to investigate drying shrinkage and cracking sensitivity subjected to restrained shrinkage of mortar containing fly ash (FA),
The coating of ZnS∶Mn by Sb-doped SnO2 using an co-precipitation process was reported. ZnS∶Mn phosphor particles were prepared by solid reaction with ZnS and
Although H.264 video coding standard provides several error resilience tools, the damage caused by error propagation may still be tremendous. This work is aimed
TiB2P/Al composite was successfully fabricated by squeeze casting technology. Its mechanical and tribological properties were evaluated. The elimination of Ti-A