考察了甲基丙烯酸锌(Zn(MAA)2)添加方式对CM性能的影响。结果表明,Zn(MAA)2用量相同时,原位生成Zn(MAA)2的胶料力学性能优于直接添加Zn(MAA)2的胶料;随着Zn(MAA)2用量的增大,
【机 构】
：
青岛科技大学 橡塑材料与工程教育部重点实验室,
论文部分内容阅读
考察了甲基丙烯酸锌(Zn(MAA)2)添加方式对CM性能的影响。结果表明,Zn(MAA)2用量相同时,原位生成Zn(MAA)2的胶料力学性能优于直接添加Zn(MAA)2的胶料;随着Zn(MAA)2用量的增大,胶料硫化程度明显提高,力学性能得到明显改善,老化后的拉伸性能保持率也得到改善;Zn(MAA)2用量在30～40份之间时,拉伸强度可达到19.7MPa,撕裂强度提高3倍以上。
The effects of zinc (Zn (MAA) 2) addition on CM performance were investigated. The results showed that the mechanical properties of in situ Zn (MAA) 2 rubber were better than that of Zn (MAA) 2 rubber with the same amount of Zn (MAA) 2. With the increase of Zn (MAA) 2, The vulcanization degree of the rubber compound is obviously improved, the mechanical properties are obviously improved, and the retention of the tensile properties after aging is also improved. When the amount of Zn (MAA) 2 is between 30 and 40, the tensile strength can reach 19.7 MPa, Increased strength more than 3 times.
其他文献
据中国橡胶网消息，日本东海炭素公司近日宣布，自7月1日起，该公司生产的所有品种炭黑售价每千克一律上调13日元（相当于每吨上涨1．3万日元）。该公司在解释提价的原因时称，日元的持续走
以聚醚多元醇(PPG-2000)/MDI体系为基础,以EG/TMP为扩链剂(扩链系数f=0.95),补加PPG-60和POP-36多元醇,采用半预聚物法合成了低硬度高回弹性浇注型聚氨酯弹性体,考察了异氰酸
离散变频软启动延用传统的软启动器结构,通过降低输出电压的频率,来提高电机的启动转矩,克服了传统软启动器不能带重载启动的弊端,但离散变频软启动不一定能在任意分频数下都
本文介绍了INTERBUS现场总线控制系统的组成和运行方式,并利用通用INTERBUS主站模块和从站模块自行构建了简单的INTERBUS控制系统。该系统使用方便、易于扩展,能够完成大多数
研究了HAAKE转矩流变仪转子转速、起始温度和混炼时间对多壁碳纳米管(MCNT)/天然橡胶(NR)复合材料力学性能的影响。结果表明,随着转子转速的增大,复合材料100%定伸应力和300%
为方便对序批式反应器(SBR)生化污水处理过程的进一步研究,探讨更有效的控制方案,根据序批式反应器(SBR)生化污水处理系统的反应机理与控制要求,构建了一个基于在线监控的SBR
采用机械共混法制备了凹凸棒土(AT)/氯丁橡胶(CR)纳米复合材料,探讨了AT用量、改性剂种类及用量和硫化剂体系等对复合材料耐磨性能的影响,还观察了使用不同改性剂制备的复合
采用丁腈橡胶/液体树脂/芳纶浆粕三元复合结构,研制了一种密封件用新型骨架材料。结果表明,该骨架材料具有工艺简便、性能优良和环境友好等特点。
Using nitrile rubber / l
分别研究了炭黑N330,炭黑N550,炭黑N660和炭黑N774对氢化丁腈橡胶(HNBR)硫化特性和力学性能的影响,并考察了4种炭黑在HNBR中的分散度和Payne效应。结果表明,炭黑N550的胶料焦
介绍了针对腈纶纺丝生产线基于PROFIBUS-DP通信的PLC控制系统的设计。该控制系统包括监控层和现场层,监控层采用MPI通信方式,现场层采用PROFIBUS-DP通信网络结构。阐述了主从