【摘 要】
：
The joining of graphite, ceramic SiC and Cf/SiC composites via preceramic silicone resin(SR) at high temperature (800-1400℃) was studied. The curing and pyroly
【机 构】
：
Key Laboratory of Advanced Ceramic Fibers and Composites
论文部分内容阅读
The joining of graphite, ceramic SiC and Cf/SiC composites via preceramic silicone resin(SR) at high temperature (800-1400℃) was studied. The curing and pyrolysis process of SR, pyrolysis temperature, inert and active fillers were especially discussed. The results show that the curing process of SR was accomplished by consuming Si-OH. The temperature of 1200℃ is the appropriate treating temperature for graphite and SiC ceramic, and the temperature of 1400℃ is suitable for Cf/SiC composites. Inert filler SiC powder(5%, mass fraction) has much positive influence on the shear strength of the joints. Active filler nano Ai, Si powder can greatly improve the properties of the joints treated at high temperature. The improvement is over 700%.
其他文献
White body-color (Y, Gd)BxV1- xO4-x :Eu3 + phosphors were prepared by coprecipitation reaction. Under VUV excitation at 147 nm, the red emission colorimetric pu
Macroporous silicon nitride (Si3N4) ceramics with high strength, uniform structure and relatively high porosity were obtained by gelcasting and carbonthermal re
Sn-Ag alloy system has been regarded as one of the most promising lead-free solder to substitute conventional Sn-Pb eutectic solder. But the formation of bulk A
Sebisty effect describes the unusual fact that the thickness of the hot-dip galvanizing coating on the steel containing 0.12%-0.25% silicon decreases with incre
A tunable dual-broad-band branch-line coupler (BLC) utilizing composite right/left-handed (CRLH) transmission lines is presented. Two λ/4 segments consisting o
MoS2 coatings were prepared by unbalanced bipolar DC magnetron sputtering under different argon pressures and for different deposition times, and the structure
Nominal composition of Ca1 - xZnxTiO3: 0. 002Pr3 + ( x = 0. 000 ～ 0. 200) phosphors were prepared by conventional solid reaction route. XRD and PL measurements w
Through the differentiating and integrating process, a mathematical model for tempering time effect on quenched steel was derived based on the attribute of stat
Application of amorphous V2O5/carbon/neodymium oxide (Nd2O3) composite is one of ways to surmount the lower electrical conductivity of V2O5. A new type of V2O5/
The variations of electrical conductivity and hardness across the thickness of an Al alloy 7010 plate under the temper condition T7651 were investigated. The el