Multiwall carbon nanotube-supported Pt (Pt/MWNTs) catalysts with high dispersion and high loading of Pt were prepared by chemical reduction method and the loading of Pt got to 40 wt%. The average diameter of Pt nanoparticles on MWNTs was about 3.5 nm. When the hydrogen and air were used as reactant gases for PEMFC, Pt/MWNTs catalysts showed significantly higher performance than the Pt/XC-72 (carbon black) catalysts.
Multiwall carbon nanotube-supported Pt (Pt / MWNTs) catalysts with high dispersion and high loading of Pt were prepared by chemical reduction method and the loading of Pt got to 40 wt%. The average diameter of Pt nanoparticles on MWNTs was about 3.5 nm. When the hydrogen and air were used as reactant gases for PEMFC, Pt / MWNTs catalysts showed significantly higher performance than the Pt / XC-72 (carbon black) catalysts.