【摘 要】
：
1985年底,我们处理了一批45钢外模零件,技术要求为HRC40～45。我们按照正常淬火工艺(820～840℃,保温15分钟,于CaCl_2中冷却)处理,结果零件几乎100％淬裂,裂纹如图示。事后,我们分
论文部分内容阅读
1985年底,我们处理了一批45钢外模零件,技术要求为HRC40～45。我们按照正常淬火工艺(820～840℃,保温15分钟,于CaCl_2中冷却)处理,结果零件几乎100％淬裂,裂纹如图示。事后,我们分别进行了金相分析和元素化验,结果金相组织为马氏体+少最残余奥氏体的正常组织,元素含量为:C0.4～0.5％;Mn0.7～0.8％;Cr0.1～0.25％。可知比正常原
By the end of 1985, we dealt with a number of 45 steel outer mold parts, technical requirements for HRC40 ~ 45. We follow the normal quenching process (820 ~ 840 ℃, holding 15 minutes, cooling in CaCl_2), the results of almost 100% quenching parts, cracks as shown. Afterwards, we carried out the metallographic analysis and elemental analysis respectively. The results showed that the microstructure was normal tissue with less martensite + less retained austenite, with the content of C0.4 ~ 0.5%, Mn0.7 ~ 0.8% Cr0.1 ~ 0.25%. Can be seen than normal
其他文献
针对铝和铝合金锻件中常见的粗晶缺陷,通过试验,对粗晶生成原因作了探讨,挤压棒中的M组织产生再结晶是粗晶生成的直接原因,设法保持挤压材料的热稳定性以防止粗晶是可行的。
本文以金相、X射线衍射和透射电镜方法研究了Fe-Mn-Al-Cr系亚稳奥氏体中形变α′-马氏体的形成,证实了它产生于ε-马氏体片相交区,且主要通过γ(?)ε(?)α′和ε(?)α′转变
当前对机械工业产品性能要求的特点是①高效率、自动化,②高速,③大负载,④高精度,⑤可靠性高,⑥节能。机械产品中有大量的摩擦付,摩擦学对机械产品的精度保持性、寿命、可
(一) 超高速的发展速度 在党的十一届三中全会方针指引下,我国的乡镇企业获得了迅速发展。1980年我国乡镇企业的总产值只有720亿元,到1984年猛增到1,709亿元,增长1.5倍,每年
为了防止铸钢件凝固过程中出现各种缺陷,尤其是缩孔、轴线缩松,保证铸件质量,必须对铸件凝固过程进行人为控制。铸钢件凝固可以归纳为两种方式,顺序凝固(又称方向性凝固)和
在实验室条件下对两种经等温淬火处理的工业球墨铸铁进行了磨粒磨损实验。并与在相同实验条件下的一系列耐磨粒磨损钢的实验结果进行了比较。结果表明,经等温淬火后的两种球
如图1所示的冲压件,一般需要两道工序;1冲孔,2翻边,需要两套单工序模具。也可在一套复合模上同时完成冲孔和翻边工序,而究竟采用什么样的复合模结构,仍需视制件的具体情况而
在过去的一年中，由于新课程改革的开始，高中语文教学已经开始呈现出新的态势。在教育部出台的《普通高中语文课程标准（实验）》中，明确提出了在拥有一定基础之后，进一步推进开放课程的相关指导办法。在这一指导办法的启发下，就诞生了人教版高中语文必修教材。在这一套教材中，把语文教学分成了名著导读、表达交流、阅读鉴赏以及梳理探究四个重要的组成部分。在更新了编写理念之后，教材的编写也适应了高中语文的实际教学。对学
测力仪是进行金属切削试验不可少的工具,并且己逐步发展为切削加工过程自动控制系统的一个组成环节。但是一台测力仪的测量与实际切削力之间总是有一定的误差,这是由于结构
国家林业局森防总站日前在京召开松材线虫病防治工作专家座谈会,来自中国科学院动物所、中国林科院森保所等单位的11名专家参加了会议。专家分析了当前松材线虫病防治工作中