Comparative study on the corrosion behavior of X52, 3Cr, and 13Cr steel in an O2–H2O–CO2 system: pro

• 作 者: Bing-wei Luo Jie Zhou Peng-pen
• 机 构: BeijingKeyLaboratoryofFailure
• 出 处: 矿物冶金与材料学报：英文版
• 发表日期: 2017年6期
• 关键词: corrosion oxygen carbon dioxide IRON CARBONATE IRON OXIDE PITTING sensitivity co
• 基金项目: financially supported by the National Natural Science Foundation of China (No. 51671215),,the Science Foundation of China University of Petroleum, Beijing (No. LLYJ-2011-41),,the Ph.D Basic Research I

The corrosion behaviors of X52, 3Cr low-alloy steel, and 13Cr stainless steel were investigated in an O2-H2O-CO2 environment at various temperatures and O2-CO2 partial-pressure ratios. The results showed that the corrosion rates of X52, 3Cr, and 13Cr stee