【摘 要】
：
200吨水压机柱塞缸的材质为45号钢(调质硬度为HB 228～280,淬火表面硬度为HRC 45～50),长达4090毫米,外径为280毫米,内径为120毫米,壁厚80毫米。因高压水的长期冲蚀,在高压水进
论文部分内容阅读
200吨水压机柱塞缸的材质为45号钢(调质硬度为HB 228～280,淬火表面硬度为HRC 45～50),长达4090毫米,外径为280毫米,内径为120毫米,壁厚80毫米。因高压水的长期冲蚀,在高压水进口处的外壁上出现了大约面积为110×300毫米,深度为1～4毫米的严重剥蚀缺陷。通过手工电弧焊修复后,该缸体运行了一年半,未在修复部位发现异常现象。修复时的补焊工艺如下:
200 tons of hydraulic machine plunger cylinder made of 45 steel (quenched and tempered HB 228 ~ 280, quenched surface hardness of HRC 45 ~ 50), up to 4090 mm, an outer diameter of 280 mm, an inner diameter of 120 mm, wall thickness 80 mm. Due to the long-term erosion of high-pressure water, severe erosion defects of about 110 × 300 mm in area and 1 to 4 mm in depth appear on the outer wall of the high-pressure water inlet. After manual arc welding repair, the cylinder was operated for a year and a half without any abnormalities found in the repair site. Repair welding repair process is as follows:
其他文献
本文采用PC—1500微机用BASIC语言编程,利用程序设计来达到直接了解单晶炉热系统各参数与熔料功率、熔料时间的关系,并对参数进行适当调整,以便一次达到实际要求值,克服了繁
中温锻造常指500—850℃温度下锻造,在此温度范围内,对常用的锻造用钢来说,一般都存在相变和再结晶现象,因此中温锻件的内在质量如何就是一个值得关心的问题。一、中温锻件
<正> 问:里根说将施行一种被称为"供应经济学"的政策,其中心内容是要在今后的三年内大量地、全面地减税.您对此有何感想?哈耶克:我还没有认真研究过那些坚持说减税就可以创造大量岁入的人的各种妙论.这种政策在英国的某种应用,恐怕还未产生这样的结果.我之所以对此种政策如此审慎,就是因为担心它可能导
尽管目前职校毕业生就业呈现供不应求的状态,但绝大多数学生或家长首选的还是普高,而分流进入职业学校的大多是普高落榜生,其中相当一部分学生不仅基础知识薄弱,又缺乏刻苦精
当代大学生存在对大学环境不适应、无法承担巨大的求职和就业压力、自我定位不准等问题。为此,可运用心理学方法和技巧,对大学生进行心理测试,大学生心理健康现状的成因进行
近几年来,镀层钢板生产取得了一些非常有意义的开发。第一,出现了用于制造容器的铬型无锡钢板(TFS—CT),即电镀氧化铬层钢板。这种产品开发后,以其成本低的特点取代了镀锡板
非洲是世界上第二个最大的原油出口地区,在国际石油贸易中占有十分重要的地位。当“石油危机”笼罩西方之际,在西方石油供应中居于举足轻重地位的非洲,更加引起西方国家的注
我厂生产汽车底盘部分铸件近二百多个品种,球墨铸铁件占94％,1984年产量近四万吨。由于球墨铸铁具有良好的铸造性能和机械性能等优点,在工业上获得了日益广泛的应用。但是,铸
用滚切法加工任意尺寸和任意截面的多头内,外螺纹(在通孔和育孔中),可确保被加工面获得较好的质量并提高生产率。在滚齿机上按照角α=α_g-α_φ角装置滚刀(参阅插图)。这里
宝钢投产前的生产准备期间,在鞍钢模拟消化了引进的油井管生产技术。试验证明引进技术是比较先进的,使钢坯收得率提高2.77%、钢管综合收得率提高3.29%、油田使用满意。此技术